Abstract:Sulfate-reducing microorganisms extensively contribute to the corrosion of ferrous metal infrastructure. There is substantial debate over their corrosion mechanisms. We investigated Fe0 corrosion with Desulfovibrio vulgaris, the sulfate reducer most often employed in corrosion studies. Cultures were grown with both lactate and Fe0 as potential electron donors to replicate the common environmental condition in which organic substrates help fuel the growth of corrosive microbes. Fe0 was corroded in cultures of a D. vulgaris hydrogenase-deficient mutant with the 1:1 correspondence between Fe0 loss and H2 accumulation expected for Fe0 oxidation coupled to H+ reduction to H2. This result and the extent of sulfate reduction indicated that D. vulgaris was not capable of direct Fe0-to-microbe electron transfer even though it was provided with a supplementary energy source in the presence of abundant ferrous sulfide. Corrosion in the hydrogenase-deficient mutant cultures was greater than in sterile controls, demonstrating that H2 removal was not necessary for the enhanced corrosion observed in the presence of microbes. The parental H2-consuming strain corroded more Fe0 than the mutant strain, which could be attributed to H2 oxidation coupled to sulfate reduction, producing sulfide that further stimulated Fe0 oxidation. The results suggest that H2 consumption is not necessary for microbially enhanced corrosion, but H2 oxidation can indirectly promote corrosion by increasing sulfide generation from sulfate reduction. The finding that D. vulgaris was incapable of direct electron uptake from Fe0 reaffirms that direct metal-to-microbe electron transfer has yet to be rigorously described in sulfate-reducing microbes.

Biogenic H 2 S and extracellular electron transfer resulted in two-coexisting mechanisms in 90/10 Cu-Ni alloy corrosion by a sulfate-reducing bacteria

Biogenic H2S and Extracellular Electron Transfer Resulted in Two-Coexisting Mechanisms in 90/10 Cu-Ni Alloy Corrosion by a Sulfate-Reducing Bacteria

Synergistic Effect of Biogenic H2s and Extracellular Electron Transfer in Microbial Biocorrosion Behavior of the 90/10 Copper-Nickel Alloy by Desulfovibrio Vulgaris: Experimental and Theoretical Research

Microbiologically influenced corrosion behavior of 70/30 Cu-Ni alloy exposed to carbon starvation environments with different aggressiveness: Pitting mechanism induced by Desulfovibrio vulgaris

Enhancement of exogenous riboflavin on microbiologically influenced corrosion of nickel by electroactive Desulfovibrio vulgaris biofilm

Microbiologically influenced corrosion of CoCrFeMnNi high entropy alloy by sulfate-reducing bacterium Desulfovibrio vulgaris

Elucidating Different Microbiologically Influenced Corrosion Behavior of Copper, 90/10 Cu-Ni Alloy, 70/30 Cu-Ni Alloy and Nickel from the Perspective of Element Content

Influence of Nutrition on Cu Corrosion by Desulfovibrio Vulgaris in Anaerobic Environment.

Corrosion of Cu by a Sulfate Reducing Bacterium in Anaerobic Vials with Different Headspace Volumes.

Carbon starvation considerably accelerated nickel corrosion by Desulfovibrio vulgaris

Investigation on the stress corrosion cracking behavior and mechanism of 90/10 copper-nickel alloy under the cooperative effect of tensile stress and Desulfovibrio vulgaris

Laboratory Investigation of the Microbiologically Influenced Corrosion (MIC) Resistance of a Novel Cu-bearing 2205 Duplex Stainless Steel in the Presence of an Aerobic Marinepseudomonas Aeruginosabiofilm

Unlocking the Effect of Interfacial Microstructure and Desulfovibrio Vulgaris on Corrosion Characteristics in Copper-Nickel Alloy Welded Joint

Studies on Sulfate Reducing Bacteria Influenced Corrosion of 90/10 Cu/Ni Alloy

Conductive magnetic nanowires accelerated electron transfer between C1020 carbon steel and Desulfovibrio vulgaris biofilm

Mitigation Effects of Ammonium on Microbiologically Influenced Corrosion of 90/10 Copper-Nickel Alloy Caused by Pseudomonas Aeruginosa

Investigation of the Mechanism and Characteristics of Copper Corrosion by Sulfate Reducing Bacteria

Electrochemical Investigation of Increased Carbon Steel Corrosion Via Extracellular Electron Transfer by a Sulfate Reducing Bacterium under Carbon Source Starvation

Microbiologically influenced corrosion of TiZrNb medium-entropy alloys by Desulfovibrio desulfuricans

Elucidating microbial iron corrosion mechanisms with a hydrogenase-deficient strain of Desulfovibrio vulgaris

Microbiologically Influenced Corrosion of Cu by Nitrate Reducing Marine Bacterium Pseudomonas Aeruginosa