Abstract:The 347H austenitic stainless steel has been widely used for pressure vessels and pipeline (PVP) applications due to its excellent creep and corrosion resistance, which fit ideally to the harsh conditions in petrochemical industries, fossil fuel or nuclear power plants, and modern energy storages. However, a failure mode has been commonly observed with cracks emerging at the heat affected zone (HAZ) of weldments during post-weld heat treatment (PWHT) or under intermediate to high temperature service conditions. This phenomenon is termed as Stress Relaxation Cracking (SRC) since the purpose of PWHT is to relieve the welding-induced residual stress fields, or as Stress Age Cracking (SAC) if failure happens during service. A leading literature explanation of this failure suggests that the residual stress relaxation and the precipitation dissolution and/or re-precipitation occur in the same temperature range, which can lead to locally high strains and thus to crack at the grain boundaries. Since in situ spatial measurements of residual stress fields, microstructural evolution, and failure processes are nearly infeasible, this work recourses to a micromechanical finite element framework that models the high temperature failure as the nucleation and growth of grain boundary cavities, whereas various parameters such as thermomechanical loading history and its evolution, the competition of grain-interior dislocation creep and grain-boundary diffusion in failure lifetime, and microstructural heterogeneities (such as the precipitate free zone near grain boundaries) can be quantitatively incorporated. It can be concluded from these microstructure-explicit simulations that an accurate knowledge of residual stress evolution and a carefully calibrated set of material constitutive parameters are the essential prerequisites for lifetime predictions. The understanding of individual governing factors also leads to a mechanistic interpretation of the observed SRC susceptibility C-curves. These results suggest that the criticality of residual stress evolution, but not the precipitation-induced local strains, be the leading factor for SRC.

Investigation on the stress corrosion cracking behavior and mechanism of 90/10 copper-nickel alloy under the cooperative effect of tensile stress and Desulfovibrio vulgaris

Microbiologically influenced corrosion behavior of 70/30 Cu-Ni alloy exposed to carbon starvation environments with different aggressiveness: Pitting mechanism induced by Desulfovibrio vulgaris

Synergistic Effect of Biogenic H2s and Extracellular Electron Transfer in Microbial Biocorrosion Behavior of the 90/10 Copper-Nickel Alloy by Desulfovibrio Vulgaris: Experimental and Theoretical Research

Unlocking the Effect of Interfacial Microstructure and Desulfovibrio Vulgaris on Corrosion Characteristics in Copper-Nickel Alloy Welded Joint

Biogenic H 2 S and extracellular electron transfer resulted in two-coexisting mechanisms in 90/10 Cu-Ni alloy corrosion by a sulfate-reducing bacteria

Biogenic H2S and Extracellular Electron Transfer Resulted in Two-Coexisting Mechanisms in 90/10 Cu-Ni Alloy Corrosion by a Sulfate-Reducing Bacteria

Laboratory Investigation of the Microbiologically Influenced Corrosion (MIC) Resistance of a Novel Cu-bearing 2205 Duplex Stainless Steel in the Presence of an Aerobic Marinepseudomonas Aeruginosabiofilm

Stress Corrosion Cracking of Copper–Nickel Alloys: A Review

In-situ Observation of Crack Initiation and Propagation in Ni-based Superalloy with Film Cooling Holes During Tensile Test

Investigation of Stress Corrosion Cracking Behavior of Super 13cr Tubing by Full-Scale Tubular Goods Corrosion Test System

Elucidating Different Microbiologically Influenced Corrosion Behavior of Copper, 90/10 Cu-Ni Alloy, 70/30 Cu-Ni Alloy and Nickel from the Perspective of Element Content

Stress Corrosion Cracking of 60/40 Cupro-Nickel Alloy: Fractography and Chemical Analysis

Investigation of microscopic residual stress and its effects on stress corrosion behavior of NiAl bronze alloy using in situ neutron diffraction/EBSD/tensile corrosion experiment

Effects of Microstructure on the Stress Corrosion Cracking Behavior of Nickel-Aluminum Bronze Alloy in 3.5% NaCl Solution

Characteristic and Mechanistic Investigation of Stress-Assisted Microbiologically Influenced Corrosion of X80 Steel in Near Neutral Solutions

Influence of Nutrition on Cu Corrosion by Desulfovibrio Vulgaris in Anaerobic Environment.

Stress Corrosion Crack of New Ultrahigh Strength Steel

Identifying Multiple Synergistic Factors on the Susceptibility to Stress Relaxation Cracking in Variously Heat-Treated Weldments

An Investigation of Corrosion-Induced Stress During SCC

Combined effect of hydrogen embrittlement and corrosion on the cracking behaviour of C110 low alloy steel in O2-contaminated H2S environment

The Effect of S2- and Stress on Pitting Corrosion of 70/30 Copper–Nickel Alloy in Seawater