Influence of texture structures of TiO2 supports on surface properties and SCR performance of V2 O5-MoO3/TiO2 catalyst
Zeying Li,Qing Tang,Zhaohong Zuo,Jun Du
DOI: https://doi.org/10.3969/j.issn.1008-1143.2016.07.008
2016-01-01
Abstract:V2O5-MoO3/TiO2( A,B,C)catalysts for selective catalytic reduction( SCR)denitrification were prepared by using the stepwise impregnation method and TiO2 support with surface area of 101.86 m2·g-1,86.37 m2·g-1,7.78 m2·g-1 respectively[denoted as TiO2(A,B,C)]. The influ-ence of TiO2 texture parameters on the catalytic properties of the catalysts for De-NOx were studied. Under the condition of GHSV 10 000 h-1 and NH3/NO volume ratio 1. 0,NO conversion over catalysts supported on TiO2(A,B)reached more than 90% at(350-450)℃,while the maximum NO conversion over the catalyst supported on TiO2( C)was only 73% at 350 ℃. Besides,the catalysts supported on TiO2( A,B) possessed better resistance performance to sulfur dioxide poisoning and lower oxidation rate of ammonia. The supports and catalysts were characterized by X-ray diffraction,N2 adsorption-desorption,UV-Vis dif-fuse reflection spectroscopy,H2 temperature-programmed reduction and NH3 temperature-programmed de-sorption. The results showed that compared with the catalysts supported on TiO2( B,C ),V2 O5 was amorphous and highly dispersed on TiO2( A)support,which would be mainly responsible for better redox property and surface acidity,subsequently the higher SCR activity.