Abstract:A series Of V2O5-TiO2 (VT) catalysts with V2O5 Contents from 15 to 75 wt% were prepared by the co-precipitation method and doped with SO42- ions. The structural properties were characterized by X-ray diffraction (XRD), Raman spectroscopy (LRS) and X-ray photoelectron spectroscopy (XPS). The surface acidity was determined by the techniques of NH3 adsorption microcalorimetry and pyridine adsorption infrared spectroscopy (FT-IR). Isopropanol (IPA) and methanol probe reactions in the presence Of O-2 were employed to provide the information about surface acidity and redox properties simultaneously. The results from XRD and LRS showed that V2O5 was well dispersed on the surface of TiO2 when the vanadia content was below 25 wt%. XPS showed that both vanadium and titanium were present in their fully oxidized states in all the samples. The SO42- doped VT samples had the sulfur oxidation state of +6. The results of NH3 adsorption microcalorimetry and pyridine adsorption FT-IR indicated that the VT catalysts possessed identical surface acid densities independently of the V2O5 content, and that both Bronsted and Lewis acid sites were present on their surfaces. The results of isopropanol probe and methanol oxidation reactions suggested that the surface acidity of VT catalysts was improved upon SO42- doping, as evidenced by the simultaneous decrease in the amounts of oxidation products and increase in the amounts of dehydration products. A high selectivity of 90% to dimethoxymethane (DMM) was measured on the SO42- modified 25% V2O5-75% TiO2 catalyst, with 54% conversion of methanol at 413 K. (c) 2007 Published by Elsevier B.V.

TiO2 Nanotubes Supported V2O5 for the Selective Oxidation of Methanol to Dimethoxymethane

Effect of acidic promoters on the titania-nanotubes supported V2O5 catalysts for the selective oxidation of methanol to dimethoxymethane

Preparation and Characterization of Mesoporous VOx–TiO2 Complex Oxides for the Selective Oxidation of Methanol to Dimethoxymethane

Selective Oxidation of Methanol to Dimethoxymethane over Iron and Vanadate Modified Phosphotungstate

Preparation of Mesoporous V–Ce–Ti–O for the Selective Oxidation of Methanol to Dimethoxymethane

Highly Selective Oxidation of Methanol to Dimethoxymethane over So42-/V2o5-Zro2

VOx Molecular Level Grafted G-C3n4 for Highly Selective Oxidation of Methanol to Dimethoxymethane

A Composite Fe–V/g-C3N4 for Liquid-Phase Selective Oxidation of Methanol with O2 Oxidant

Surface and Catalytic Properties of V2O5–TiO2/SO42− Catalysts for the Oxidation of Methanol Prepared by Various Methods

Copper Vanadate Nanowires on G-C3n4 Toward Highly Selective Oxidation of Methanol to Dimethoxymethane

Investigation on C–TiO2 Nanotubes Composite As Pt Catalyst Support for Methanol Electrooxidation

TiO<sub>2</sub> Nanotube Film as the Support of Platinum Electro-Catalyst with Enhanced Electrochemical Activity for Methanol Oxidation

Selective oxidation of methanol to dimethoxymethane under mild conditions over V2O5/TiO2 with enhanced surface acidity.

Tio2 Nanotube Film As the Support of Platinum Electro-Catalyst with Enhanced Electrochemical Activity for Methanol Oxidation

TiO2 Nanotube-Carbon (TNT-C) as Support for Pt-based Catalyst for High Methanol Oxidation Reaction in Direct Methanol Fuel Cell

Structural, Acidic and Redox Properties of V2O5-TiO2-SO42− Catalysts

Plasma-induced Synthesis of Pt Nanoparticles Supported on TiO 2 Nanotubes for Enhanced Methanol Electro-Oxidation

The Effect of TiO 2 on the Catalytic Activity of a PtRu/C Catalyst for Methanol Oxidation

Influence of the Metal Oxide Support on the Surface and Catalytic Properties of Sulfated Vanadia Catalysts for Selective Oxidation of Methanol

Investigation of the Structure and Active Sites of TiO2 Nanorod Supported VOx Catalysts by High-Field and Fast-Spinning 51V MAS NMR

Pt Nanoparticles Supported on Non-Carbon Titanium Chromium Nitride Nanotubes with High Activity and Durability for Methanol Oxidation Reaction