Abstract:One-dimensional (1-D) antimony-doped tin oxide nanofibers (ATO NF) were synthesized with the electrospinning method and were employed as Pt catalyst support materials for the methanol oxidation reaction (MOR). Scanning and transmission electron microscopy (SEM/TEM) indicate that the ATO NF exhibits a porous nanofiber structure and the diameters are in the range of 100 to 150 nm consisting of the stacked small ATO nanoparticles. Uniformly dispersed Pt nanoparticles were then deposited onto the ATO NF and the synthesized ATO nanoparticles (ATO NP) with a Pt loading of 20 wt%. Compared with the commercial Pt/C catalysts, both the ATO NF– and ATO NP–supported catalysts showed slightly lower electrochemical surface areas (ECSA) and catalytic activity towards the MOR. However, ATO NF, when used as Pt support, showed enhanced MOR stability. This enhancement is mainly attributed to the greater corrosion resistance and porous nanofiber nature of the ATO NF, which tend to inhibit the aggregation of anchored Pt nanoparticles and reduce the loss of ECSA during the accelerated life test. XPS results also indicate strong interactions between platinum and ATO particles, which in turn significantly enhance stability towards MOR.Graphical AbstractPorous ATO nanofibers are synthesized as a support for Pt by the electrospinning method. Such prepared catalyst exhibits enhanced catalytic stability for MOR compared with ATO NP and Pt/C.

TiO2 Nanotube-Carbon (TNT-C) as Support for Pt-based Catalyst for High Methanol Oxidation Reaction in Direct Methanol Fuel Cell

Highly Active Nanoporous Pt-based Alloy As Anode and Cathode Catalyst for Direct Methanol Fuel Cells

TiO<sub>2</sub> Nanotube Film as the Support of Platinum Electro-Catalyst with Enhanced Electrochemical Activity for Methanol Oxidation

Tio2 Nanotube Film As the Support of Platinum Electro-Catalyst with Enhanced Electrochemical Activity for Methanol Oxidation

f Pt nanoparticles supported on anatase TiO 2 nanotubes with good photo-electrocatalysis performance for methanol †

Methanol Oxidation over Tio2-Modified Multi-Walled Carbon Nanotubes Supported Pt-Mo Electrocatalyst

Methanol Oxidation at Platinum Coated Black Titania Nanotubes and Titanium Felt Electrodes

Facile synthesis of Pt nanoparticles supported on anatase TiO2 nanotubes with good photo-electrocatalysis performance for methanol

Plasma-induced Synthesis of Pt Nanoparticles Supported on TiO 2 Nanotubes for Enhanced Methanol Electro-Oxidation

A Comparative Investigation of the Electrocatalytic Oxidation of Methanol on Pt Modified TiO2 Nanotube Electrodes with Two Methods

Carbon-Coated and Interfacial-Functionalized Mixed-Phase Mox Ti1-x O2-δ Nanotubes as Highly Active and Durable PtRu Catalyst Support for Methanol Electrooxidation

PtRu Catalysts on Nitrogen-Doped Carbon Nanotubes with Conformal Hydrogenated TiO 2 Shells for Methanol Oxidation

TiO2 Nanotubes Promoting Pt/C Catalysts for Ethanol Electro-Oxidation in Acidic Media

Multi-walled carbon nanotubes modified by sulfated TiO2 – A promising support for Pt catalyst in a direct ethanol fuel cell

N-doped titanium oxide/carbon composite as supports for platinum catalysts in highly efficient methanol oxidation

Lattice distortion of PtCo nanoparticles encapsulated in TiO 2 nanotubes boosts methanol oxidation

Ordered Nio-Tio2 Nanotube Arrays As an Efficient Catalyst Support for Methanol Oxidation

Antimony-Doped Tin Oxide Nanofibers as Catalyst Support Structures for the Methanol Oxidation Reaction in Direct Methanol Fuel Cells

Excellent dispersion and electrocatalytic properties of Pt nanoparticles supported on novel porous anatase TiO2 nanorods

Pt supported on phosphorus-doped carbon nanotube as an anode catalyst for direct methanol fuel cells

Carbon-Supported Pt and Ptru Nanoparticles As Catalysts for A Direct Methanol Fuel Cell