Abstract:Due to the high activation energy barrier and the sporadic nature of nucleation, the temperature required for the transition from cubic dense γ-Al2O3 to tripartite α-Al2O3 is as high as 1100–1200 °C. In this work, a two-step strategy was employed to reduce the phase transformation temperature, and prepare α-Al2O3 particles with good dispersion. As the first step, 10 nm sheet γ-Al2O3 was obtained by ammonium aluminum carbonate (AACH) decomposition, which was more favorable to the crystal transformation in the next ball-milling processing. In the second step, γ-Al2O3 powder with partial α-Al2O3 produced in situ by ball-milling γ-Al2O3 was calcined, and α-Al2O3 nanoparticles were obtained at just 850 °C. The content of the α-Al2O3 is determined by the Rietveld Refine method. The relationship between ball-milling time and α-Al2O3 content was clarified, and the effect of α-Al2O3 content on the transformation temperature and morphology of γ-Al2O3 was discussed. The results showed that the α-Al2O3 content rises with the increase of ball milling time, and spherical α-Al2O3 nanoparticles can be obtained when the α-Al2O3 content is 5 %. The addition of α-Al2O3 seeds reduces the phase transition temperature but agglomeration exists. Our proposed two-step low-temperature calcination strategy is an important method for the preparation of alumina nanoparticles

Preparation of High Pure and Micron-Sized α-Al2O3 Powder by Activated Aluminium Hydrolysis Method

Hydrothermal Preparation of CuAlO2 Powder

PURIFICATION OF TAN RAI ALUMINUM HYDROXIDE WITH ACETIC ACID AND PREPARATION OF HIGH PURE NANOSIZE α-ALUMINA

Synthesis and phase formation mechanism of alpha-Fe2O3 powders by hydrothermal reaction method

Study on ultrasound-assisted preparation of sphere-like high-purity alumina

Preparation of NiAl2O4/Al2O3 composite nanopowder

Synthesis of Nano-Alumina Hydroxide Sol Using Sol-gel Method

Preparation of Ag-Al2O3 nano-composites powder

Preparation and Catalytic Property of Single Crystal Multiporousα-Fe_2O_3 Nanorods

Lowering the synthesis temperature of α‐Al2O3 by increasing the content of pentacoordinate aluminum in the precursors

Preparation of High-purity Alumina via Hydrolysis of Aluminum Isopropoxide after Desilication with Lanthanum Oxide

Preparation of Micro/nano Sized AI2O3 Using the By-product of Al-based Composites Hydrolysis Reaction

Preparation of Self-Healing Α-Al2o3 Films by Low Temperature Thermal Oxidation

Preparation of Fineα-Al_2O_3 Powders by Calcining Carbon-coveredγ-Al_2O_3 in Oxygen

Preparation of MoO 3 powder by hydrothermal method

Future Application of the Preparation Al_2O_3 Nanometer by Hydrothermal Method

OPTIMIZATION OF HEAT TREATMENT TECHNOLOGY OF NANO Al2O3 POWDERS

Preparation of High-Purity Aluminum Oxide via Mechanochemical Oxidation of Aluminum in a 0.1 M KOH Solution, Followed by Chemical and Heat Treatments

Preparation And Characterization Of Gamma-Al2o3 By Polyaluminum Chloride With High Al-13 Content

Mechanism of Hard Agglomerate Formation in a High Purity Sub-micron α-Alumina Powder

Preparation of α-Al2O3 by low-temperature calcining γ-Al2O3 with α-phase seed in-situ obtained by ball milling