Abstract:The high temperature compressive tests of squeeze casting ZK60 magnesium alloy in the testing temperature range of 523-723K and strain rate range of 0.001-10s-1 were performed on Gleeble-1500D thermal simulator testing machine. Optical microscopy was performed to elaborate on the dynamic recrystallization (DRX) grain growth. TEM observation indicated that the mechanical twinning, dislocation slip, and dynamic recrystallization are the materials typical deformation features. Variations of flow behavior with deformation temperature as well as strain rate were analyzed. Analysis of the flowing deformation behavior and microstructure observations indicated that the flow localization was observed at lower testing temperature and higher strain rates. Dynamic recrystallization occurred at higher testing temperature and moderate strain rates, which improved the ductility of the material. The results indicated that at the testing temperatures lower than 573K and strain rates higher than 1s-1, the material exhibited flow instability manifesting as bands of flow localizations. These temperatures and strain rates should be avoided in processing the material. Dynamic recrystallization occurs in the temperature range 573-723K and the strain rate range 0.001-0.1s-1. The number of dynamic recrystallization grains is less at lower temperature and higher strain rate than higher temperature and lower strain rate. The dynamic recrystallization is inadequate at 573-623K while the dynamic recrystallization grain growth has been observed in the temperature range of 673-723K. Therefore it may be considered that the optimum processing parameters for hot working of squeeze casting ZK60 magnesium alloy are 648K and 0.001-0.01s-1, at which fine dynamic recrystallization microstructure can be obtained.

Plastic Deformation at High Temperature and Processing Map of AZ61 Magnesium Alloy

Hot Deformation Behavior and Processing Map of As-Cast AZ61 Magnesium Alloy

Plastic Deformation at Elevated Temperature and Processing Maps of Magnesium Alloy

Analysis on Processing Map of AZ31 Magnesium Alloy

Hot Deformation and Processing Map of As-Homogenized Mg–9Gd–3Y–2Zn–0.5Zr Alloy

Construction of Hot Processing Map, Dynamic Recrystallization Critical Conditions and Kinetic Model of AZ61 Alloy

Processing Map and Kinetic Analysis for Hot Deformation of an As-Cast AZ91D Magnesium Alloy

Processing Map for Hot Working of As Extruded AZ31B Magnesium Alloy

Hot Deformation Behavior and Processing Map of Squeeze Cast Zk60 Magnesium Alloy

3D Processing Map for Hot Working of Extruded AZ80 Magnesium Alloy

Processing maps for hot working of ZK60 magnesium alloy

Deformation Behavior of ZK60 Magnesium Alloy at Elevated Temperature

Hot deformation behavior of as-Cast AZ61 magnesium alloy

Plastic Deformation Behaviors and Dynamic Recrystallization Mechanisms of ZK60 Magnesium Alloy

Hot Deformation Behavior and Processing Map of Al-Zn-Mg-Cu-Zr Alloy

Hot Deformation Behavior and Workability of Pre-Extruded ZK60A Magnesium Alloy

Hot Processing Maps and Hot Deformation Behavior of As-cast AZ80A Magnesium Alloy

Effect of Strain,strain Rate and Temperature on Workability of AZ80 Wrought Magnesium Alloy

Hot Deformation Behavior and Processing Map of Al-Zn-Mg-Sc-Zr Alloy

Compressive Deformation of ZK60 Magnesium Alloy at Elevated Temperature

Characterization of Hot Deformation Behavior of As-Homogenized Al–Cu–Li–Sc–Zr Alloy Using Processing Maps