Analysis of high-temperature deformation and microstructure of an AZ31 magnesium alloy
S. Spigarelli,M. El Mehtedi,M. Cabibbo,E. Evangelista,J. Kaneko,A. Jäger,V. Gartnerova
DOI: https://doi.org/10.1016/j.msea.2006.03.155
2007-07-01
Abstract:High-temperature plastic deformation and dynamic recrystallization of AZ31 extruded (EX) and heat treated (FA) alloy was investigated in the temperature range between 200 and 400°C. High-temperature straining resulted in partial dynamic recrystallization above 250°C; in the EX alloy recrystallization was complete at 300°C, while a moderate grain growth was observed at 400°C. The peak flow stress dependence on temperature and strain rate are described by means of the conventional sinh equation; the calculation of the activation energy for high temperature in the whole range of temperature deformation gives Q=155kJ/mol, i.e. a value that was reasonably close but higher than the activation energy for self diffusion in Mg. The microstructure resulting from high-temperature straining was found to be substantially different in EX and FA alloys; in particular, the EX alloy was characterized by a lower flow stress, a higher ductility and by a finer size of the dynamically recrystallized grains. These results are then discussed on the basis of the “necklace” mechanism of dynamic recrystallization.
materials science, multidisciplinary,nanoscience & nanotechnology,metallurgy & metallurgical engineering