Abstract:This research explored effect of steam curing on strength, durability and microstructure of concretes with and without mineral admixtures of fly ash (FA) and ground granulated blast furnace slag powder (SL). The two types of C55 strength grade concretes (one is pure cement concrete, another one is concrete, replacing part of cement with 12% FA and 18% SL) were prepared and their compressive strength, chloride diffuse on coefficient and carbonation depth under the standard and steam curing conditions were measured and compared. The phase composition and microstructure of the concretes under the two curing conditions were tested by X-ray diffraction (XRD), scanning electron microscope (SEM) and mercury intrusion porosimeter (MIP). The results show that, on the one hand, compared with standard curing, steam curing is beneficial to the early strength, but not conducive to the later strength development and chloride permeability resistance of both two types of concretes. Furthermore, for the steam cured concrete, the 28d carbonation depth of the forming surface is higher than that of the bottom surface. What's more, steam curing can reduce the carbonization resistance of pure cement concrete and improve the carbonization resistance of concrete mixed with FA and SL. On the other hand, composite mineral admixtures of FA and SL reduce the early strength, the carbonization resistance of concrete cured with standard curing, but improve the later strength, the carbonization resistance and chloride permeability resistance of concrete cured with steam curing. FA and SL are thermally activated under steam curing and can react with the calcium hydroxide formed by cement hydration in the early stage, which produces larger amount of secondary hydration products to improve the pore structure and interfacial microstructure of the concrete with FA and SL. Thus, the adverse effects of steam curing on later strength and durability of concrete are significantly restrained by composite mineral admixtures of FA and SL.

Study on Strength, Shrinkage and Creep of Concrete Containing Ultrafine Fly Ash Composites

Shrinkage and Creep of Sustainable Self-Compacting Concrete with Recycled Concrete Aggregates, Fly Ash, Slag, and Silica Fume

Effects of ultrafine fly ash on the properties of high-strength concrete

Research on Improving Cementitious Material Properties by Adding FineFly Ash

The Research of the Effect of Fly Ash on the Shrinkage Property of Commercial Concrete

Compressive, flexural and splitting strength of fly ash and silica fume concrete

Experimental study on the compressive strength and shrinkage of concrete containing fly ash and ground granulated blast‐furnace slag

Study on performance of high strength pumping concrete compounded by fly ash composite powder under low water-cement ratio

Mechanical properties and micro-structure analysis of concrete adding high performance composite cementious material

lnfluence of steel slag - superfine fly ash composite mineral admixture on the properties of concrete

Influence of Fly Ash on the Compressive Strength of Concrete under Temperature Match Curing Conditions

Microstructure of the concrete with high volume of fly ash-at the long-term age

Compressive strength, flexural strength, and durability of high-volume fly ash concrete

The Influence of Fly Ash Addition on the Autogenous Shrinkage of High-Strength Concrete

Hydration, mechanical properties and durability of high-strength concrete under different curing conditions

Effect of steam curing on strength, durability and microstructure of concretes with and without mineral admixtures

Study on Mechanics Property Experiments of High Fly Ash Content Concrete

Experimental Study on the Cracking Resistance at Early Ages of High Performance Concrete Added with Lithium Slag and Fly Ash

Compressive behavior and microstructural analysis of low and high volume fly ash concrete containing recycled concrete aggregate

Effects of Blended Steel Slag-Superfine Fly Ash Mineral Admixture and Ordinary Fly Ash on the Properties of Concrete

Effect of Curing Regime on the Mechanical Properties and Durability of Steam Cured-Concrete