Abstract:This present study mainly focuses on the influence of low-calcium circulating fluidized bed fly ash (LCFA) on the mechanical property and microstructure of cement-based materials under different curing conditions. The mechanical properties test was conducted by changing variable parameters, such as LCFA content, the internal mixing ratio of LCFA and fly ash (FA), and dry and water curing conditions. Further, the hydration products and pore structure were analyzed using XRD, FT-IR, TG-DTG, NI, SEM, and BET micro-testing technology. The strength development law of LCFA on cement-based materials is discussed. The research results show that LCFA has a certain degree of self-hardening and can be used as a cementitious material in cement-based materials. Still, the loose and porous microstructure of LCFA leads to higher water requirements, which reduces the fluidity of cement-based pastes. Water curing is favorable for promoting the development of LCFA on the long-term compressive strength of cement-based materials. When the LCFA was added to the cement, the optimal substitution ratio was 20%, and the compressive strength at 91 days reached 101 MPa. In the case of compounding LCFA and FA, when the internal mixing ratio of LCFA/FA was 3 and the total content was 20%, the mechanical properties were the highest, and the compressive strength at 91 days was 92 MPa. The microscopic analysis result shows that the cumulative hydration heat of the samples decreased significantly with the increase of dosage of LCFA. The main hydration products of cement-based materials mixed with LCFA were AFt, C-S-H gel, and Ca(OH)2. AFt and C-S-H gels are critical to the strength development of OPC-LCFA samples. The active Al2O3 and active SiO2 in LCFA were involved in hydration reactions to promote the formation of C-A-H and C-S-H gel and effectively promote the development of the mechanical properties. Overdosages of LCFA would reduce the ettringite formation rate. FA is not conducive to AFt formation in the hydration process of OPC-FA samples.

Compressive behavior and microstructural analysis of low and high volume fly ash concrete containing recycled concrete aggregate

Study on the Effect of Fly Ash and Polycarboxylic Acid Water Reducer on the Properties of Recycled Concrete

Shrinkage and Creep of Sustainable Self-Compacting Concrete with Recycled Concrete Aggregates, Fly Ash, Slag, and Silica Fume

Development of Sustainable Self-Compacting Concrete Using Recycled Concrete Aggregate and Fly Ash, Slag, Silica Fume

Influence of Construction Conditions on Properties of Recycled Concrete

Circulation Fluidized Bed Combustion Fly Ash as Partial Replacement of Fine Aggregates in Roller Compacted Concrete

Investigation of Low-Calcium Circulating Fluidized Bed Fly Ash on the Mechanical Strength and Microstructure of Cement-Based Material

Mixture Design and Mechanical Properties of Recycled Mortar and Fully Recycled Aggregate Concrete Incorporated with Fly Ash

Study of Mechanical Properties of an Eco-Friendly Concrete Containing Recycled Carbon Fiber Reinforced Polymer and Recycled Aggregate

Synergetic Effect of Fly Ash and Ground-Granulated Blast Slag on Improving the Chloride Permeability and Freeze–thaw Resistance of Recycled Aggregate Concrete

Recycling of the end-of-life lightweight aggregate concrete (LWAC) with a novel approach

Study on the Effect of Supplementary Cementitious Material on the Regeneration Performance of Waste Fresh Concrete

Effect of Fly Ash on the Mechanical Properties and Microstructure of Cement-Stabilized Materials with 100% Recycled Mixed Aggregates

Experimental study on the compressive strength, damping and interfacial transition zone properties of modified recycled aggregate concrete

Micro-structure Characteristics of Recycled Fine Aggregate and Its Concrete

Fresh and hardened properties of recycled plastic fiber reinforced self-compacting concrete made with recycled concrete aggregate and fly ash, slag, silica fume

Sustainable Concrete: Exploring Fresh, Mechanical, Durability, and Microstructural Properties with Recycled Fine Aggregates

Optimization of the preparation process of Fair-Faced concrete incorporating recycled aggregates

Effect of Recycled Fine Aggregates on the Mechanical and Drying Shrinkage Properties of Alkali-Activated Recycled Concrete

Influence of Mineral Additions on the Anti-Cracking Performance of Recycled Aggregate Concrete

Sustainable self-compacting concrete containing high-amount industrial by-product fly ash as supplementary cementitious materials