Corrosion Behaviour of Three Kinds of Arc Sprayed Coatings in Soil
Jialiang Song,Zhaoliang Li,Dongjiu Zhang,Qiong Yao,Ziheng Bai,Yali Feng,Chaofang Dong,Kui Xiaol
DOI: https://doi.org/10.20964/2019.12.60
IF: 1.541
2019-01-01
International Journal of Electrochemical Science
Abstract:The corrosion resistance of a pure Zn coating, a ZnAl alloy coating and a ZnAl pseudo-alloy coating in a Beijing area was studied. The corrosion products were analysed by XRD, and the electrochemical processes of the three coatings were analysed by measuring the electrochemical impedance and polarization curves. The results showed that the surface corrosion products of the pure Zn coating were mainly composed of Zn-5(OH)(8)Cl2H2O, ZnCO3, ZnO and Zn-5(CO3)(2)(OH)(6), while the surface corrosion products of the ZnAl alloy and ZnAl pseudo-alloy coating similarly consisted of Zn-5(OH)(8)Cl2H2O, Zn0.71Al0.29(OH)(2)(CO3) 0.145xH(2)O and ZnO center dot Al2O3. Before and after corrosion, the order of the coating corrosion resistance was as follows: ZnAl alloy coating > ZnAl pseudo-alloy coating > pure Zn coating. It was found that a "self-sealing" protective effect of the ZnAl alloy coating was better than that of the ZnAl pseudo-alloy coating because the composition was more uniformly distribution. The main reason for a weaker "self-sealing" protective effect of the ZnAl pseudo-alloy was that galvanic corrosion occurred between the Zn-rich phase and the Al-rich phase of the pseudo-alloy, which accelerated the electrochemical reaction. Meanwhile, the pure Zn coating did not have the "self-sealing" effect. Consequently, the corrosion resistance of the ZnAl alloy coating was the best.