Abstract:Superhydrophobic coatings with high strength and corrosion resistance on hard metal surfaces have been attracting significant attention in recent years. In this paper, a quick and easy method using Fe-based micro/nano composite electro-brush plating and subsequent modification with stearic acid was established for fabricating superhydrophobic surfaces on A3 steel plates. The processing parameters including the working voltage, the brushing speed and the micro-TiO2 particle concentration were studied to determine their influences on the wettability. A blackening process was conducted to further improve the corrosion resistance of the Fe-based plating layer with high water repellency. The surface morphology and chemical composition were analyzed by scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS). Corrosion resistance ability was measured using an electrochemical workstation. The results suggested that: the rough structure of the superhydrophobic coatings can be successfully fabricated by electro-brush plating technology with appropriate parameters; after post-treatment by stearic acid, the contact angle of the composite coating was up to 156 degrees and the sliding angle was even as low as 1 degrees under the optimal process. Meanwhile blackening treated superhydrophobic coatings still maintained excellent superhydrophobicity and the self-corrosion potential improved by 0.116 V compared to the untreated brush plating layer and the prepared superhydrophobic coatings achieved an excellent long term anti-corrosion performance.

Study on Corrosion Resistance of the A3 Steel Treated by a Water-borne Silicone Emulsion

The Preparation of Coatings with Codepositon Plating on A3 Steel and Its Corrosion Resistance

EFFECT OF SOLUBLE SALTS ON UNDERFILM CORROSION AND FAILURE OF COATINGS OF A3 STEEL

Study of the Corrosion Behavior of A3 Carbon Steel in Simulated Oilfield Water

Corrosion mechanism of A3 steel induced by chloride ions in the purified water

Study on Corrosion Resistance of Hot Dip Al-Zn Steel Pretreated with Bis-(triethoxysilylpropyl) Tetrasulfide

Effect of Mixture Ratio on Water Uptake and Corrosion Performance of Silicone-Epoxy Hybrid Coatings Coated 2024 Al-alloy

Sealing Effects Of Silica Sol Modified Waterborne Acrylic Resin On Chromium Trivalent Passivation Film Of Galvanized Steel

Corrosion Inhibition of A3 Steel by Imidazoline Derivative in 2·0%nacl Solution

Study on the Electrochemical Corrosion Behavior of A3 Steel in Eutrophic Fresh Water

Research on Preparation of Silane Film on the Surface of Carbon Steel and its Property of Corrosion Resistance

Effect of surface films prepared by IBAD on corrosion resistance of plant steel A3

Inhibition performance of an imidazoline containing carboxyl moiety for A3 steel in oilfield wastewater

Preliminary Study on the Corrosion Behavior of A3 Steels in Polluted Freshwater

Effect of Heat Treatment on Corrosion Resistance of A3 Steel in Sodium Bicarbonate Solution

IMIDAZOLINESON'S CORROSION INHIBITION IN ACIDE SOLUTION FOR A3 STEEL

Corrosion rates of A3 steel in polymer flooding produced liquids

Corrosion inhibition capacity of non-phosphorus corrosion inhibitor in water with moderate alkalinity and moderate hardness for A3 carbon steel

Ionic Synergistic Effect of the Anionic/Cationic surfactant for Corrosion Inhibition of A3 Carbon Steel

Corrosion protection investigations of oxide‐silane composite coating on hot dip aluminized steel

Preparation of anti-corrosion superhydrophobic coatings by an Fe-based micro/nano composite electro-brush plating and blackening process