High-Temperature Corrosion Resistance of Electroplated Ni-Al Composite Coating Prepared on Mild Carbon Steel Form a Water-Based System

陈尚东,孙挺,王传胜,李婷婷

DOI: https://doi.org/10.16577/j.cnki.42-1215/tb.2009.08.027

2009-01-01

Abstract:A nickel sulfate hath was used to prepare pulse electroplated coating of Ni-wrapped Al powder on the surface of A3 steel, which was conducted based on optimizing the composition of the plating bath and electroplating parameters. The adhesion to substrate, porosity, and antioxidation behavior of the coating were investigated, while its microstructure was analyzedby means of scanning electron microscopy and X-ray diffraction. Results show that the pulsed electroplated composite coating has much better corrosion resistance and antioxidalion ability at elevated temperature than the coating prepared by direct current electropla-ting. And it is composed of regularly-shaped grains and has strong intergranular bonding. Moreover, the pulsed electroplated coating is even and integrated and has better adhesion to substrate as com-pared to the coating prepared by direct current electroplating. At the same time, Ni-A1 intermctallics were formed after the pulsed e-lectroplated coating was heat treated at elevated temperature as a surface protective film, which contributes to improved corrosion re-sistance of the steel substrate at elevated temperature.