Abstract:Swing-arc narrow gap GMA vertical-up welding is a high-efficiency technique. However, typical lack-of-fusion defect could still exist. We tried to clarify the forming mechanism of the typical defects. Experiments of EH40 grade steels under various processing parameters were carried out in this study. Processual phenomena of molten behavior and arc stability were described and analyzed by synchronously collecting and counting the high-speed graphic and electronic features of the welding procedure. Effects of traveling speed, swing amplitude (α), sidewall staying time (ts), and the peak pulsed voltage (Up) on the metal transfer, statistical characteristics of the max pulsed current (Ip) and the wire tip position, and weld formation were investigated. The tendency and the forming mechanism of the lack-of-fusion defect were investigated. It is realized that a relatively fast traveling speed would increase the tendency of a convex bead and make the arc more divergent in the swinging period, which would increase the trend of interlayer lack-of-fusion defect. The change of any parameter among α, ts, and Up which makes the Ip-value distribution much above the threshold globular-spray transfer Ip-value range would lead to a deviation from the stable pattern of the wire-tip trajectory and a severe climbing on a certain sidewall. The sidewall lack-of-fusion defect usually occurs on the other side after the severe climbing on the previous side. The continuous arc premature climbing onto the sidewall during the swinging period causes the sidewall lack-of-fusion defect.

Effects of Wire Rotating Frequency on Metal Transfer Process in Rotating Arc Narrow Gap Horizontal Gmaw

Metal Transfer Characteristics of Rotating Arc Narrow Gap Horizontal GMAW

Effect of Rotating Arc Process on Molten Pool Control in Horizontal Welding

Study on weld formation in a novel rotating arc horizontal GMAW

Effect of high-frequency phase shift on metal transfer and weld formation in aluminum alloy double-wire DP-GMAW

Characteristics of the Electrode Melting Phenomena in Narrow Gap Mag High-Rotating-Speed Arc Welding

Effects of Processing Parameters on Molten Behavior, Arc Stability, and Defect Forming in Swing-Arc Narrow Gap GMA Vertical Up Welding

Effects of Welding Velocity on Metal Transfer Mode and Weld Morphology in Underwater Flux-Cored Wire Welding

A novel rotating wire GMAW process to change fusion zone shape and microstructure of mild steel

Effect of Forces on Dynamic Metal Transfer Behavior of Cable-Type Welding Wire Gas Metal Arc Welding

Study of metal transfer control in underwater wet FCAW using pulsed wire feed method

Application of Rotating Arc System to Horizontal Narrow Gap Welding

Effects of process parameters on the depth-to-width ratio of flux-cored wire underwater wet welding

Effect of metal transfers and shielding gases on profiles of high current MAG welding

Stirring effect of the rotating arc on the molten pool during non-axisymmetric tungsten NG-GTAW

Influence of Interwire Angle on Undercutting Formation and Arc Behavior in Pulsed Tandem Narrow-Gap GMAW

Effect of magnetic field frequency on the shape of GMAW welding arc and weld microstructure properties

Study on Forming Mechanism of Appearance Defects in Rotating Arc Narrow Gap Horizontal GMAW

Effect of Water Flow on the Arc Stability and Metal Transfer in Underwater Flux-Cored Wet Welding

Metal transfer characteristics of GMAW with strip electrode

Rotating arc horizontal narrow gap welding of high strength quenched and tempered steel