Abstract:This study reports the formation of Er-doped nanocrystalline cobalt ferrite with the formula CoFe2-x Er x O4 (0.0 ≤ x ≤ 0.10) from nontoxic metal precursors Co(NO3)2·6H2O, Fe(NO3)3·9H2O, and Er(NO3)3·5H2O through an easy and economical sol-gel route in which citric acid is served as the chelating agent. The as-prepared powder was annealed at 700 °C for 3 h in ambient air to get the required spinel structure. The annealed samples were subjected to structural and magnetic characterization. The X-ray diffraction (XRD) data of the samples confirmed the cubic spinel structure formation. The average crystallite size evaluated from XRD data increased from 21 to 34 nm with the substitution of Er due to the larger atomic size of Er3+ than Fe3+. Moreover, the crystallite size obtained from XRD data are well matched with the particle size measured from transmission electron microscopy images. The lattice parameters obtained from XRD data agree well with the values estimated from theoretical cation distribution and Rietveld refinement calculation. The hysteresis curve exhibits the particles are soft ferromagnetic and the coercivity increased from 54.7 to 76.6 kA/m with maximum saturation magnetization, M s = 61 emug-1 for 0.10 Er content. The squareness ratios were found to be less than 0.5, which indicates the single-domain nature of our particles. The blocking temperature measured from field cooled-zero field cooled curves is T B > 350 K for all the samples, which is much higher than the room temperature (300 K). The enhancement of saturation magnetization and coercivity has been explained based on the crystallite size, anisotropy constant, and cation distribution. Thus, the structural and magnetic properties of CoFe2O4 nanoparticles (NPs) can be tuned by Er incorporation and these NPs can be applied in different soft magnetic devices.

Surface Morphology and Magnetic Properties of CoFe2O4 Thin Films Prepared via Sol–Gel Method

The Sol-Gel Preparation and Afm Study of Spinel Cofe2o4 Thin Film

Morphology and magnetic properties of Co0.8Fe2.2O4 films prepared by the chemical solution deposition

Synthesis of Nanocrystalline Ferrites Zn0.4ni0.6cr0.5laxfe1.5-Xo4 and Its Magnetic Properties

Structure And Magnetic Properties Of Co2.73fe0.27o4 Synthesized By The Heat-Decomposition Method

Growth of Textured CoFe 2 O 4 Thin Films on Platinized Silicon Prepared by a Sol-Gel Method

Chemical Synthesis and Magnetic Study of Nanocrystalline Thin Films of Cobalt Spinel Ferrites

Sol–gel Synthesis, Magnetic and Magneto-Optical Properties of CoFe2−xTbxO4 Nanocrystalline Films

Sintering-dependent mechanical and magnetic properties of spinel cobalt ferrite (CoFe2O4) ceramics prepared via sol-gel synthesis

Magnetic properties and magnetism simulation of SmFe0.5Cr0.5O3 nanoparticles prepared by sol-gel method

Structural, Magnetic, and Dielectric Properties for Mg0.6Co0.2Cu0.2FeCrO4 Spinel Ferrites Prepared Under Different Calcination Temperatures

Nanostructured Magnetite (fe3o4) Thin Films Prepared by Sol–gel Method

Preparation and magnetic properties of CoFe2O4 nanowires

Magnetism and Phase Transition for CoFe2−xMnxO4 Nanocrystalline Thin Films and Powders

Microstructure, magnetic and magneto-optical properties of Co-Mn ferrite nanocrystalline films

Magnetic Properties of Sputtered Fe1−xO and Fe+Fe3O4 Thin Films

Magnetically Hard Face-Centered-tetragonal FePt Film Prepared by Sol–gel Spin Coating

Magnetism of CoFe2O4 Thin Films Annealed under the Magnetic Field

Synthesis of CoFe2O4 Nanoparticles via Solution Method and Their Magnetic Properties

Calcination effects on the crystal structure and magnetic properties of CoFe2O4 nanopowders synthesized by the coprecipitation method

Sol-Gel Route for the Synthesis of CoFe2- x Er x O4 Nanocrystalline Ferrites and the Investigation of Structural and Magnetic Properties for Magnetic Device Applications