Abstract:Co magnetic films are widely used in high-frequency magnetic recording and vertical magnetic recording due to their high saturation magnetization and magnetocrystalline anisotropy. In this work, ferromagnetic Co magnetic films were prepared on copper substrate by vacuum evaporation combined with heat treatment (H2 atmosphere), to investigate the impact of film thickness and annealing temperature on microstructure and magnetic properties. The results show that with the increase in annealing temperature, the Co thin film physical phase does not change significantly, the crystallinity increases, and the grain size increases, which is consistent with the results obtained from the SEM morphology map of the sample surface, leading to an increase in coercivity. By annealing experiments (atmospheric atmosphere) on Co magnetic films with and without an Al protective layer, as shown by scanning electron microscopy microscopic characterization results, it was verified that the Al layer can protect the inner Co layer from oxidation. As the film thickness increases from 10 to 300 nm, the magnetic properties of Co films change significantly. The saturation magnetization gradually increases from 0.89 to 5.21 emu/g, and the coercivity increases from 124.3 to 363.8 Oe. The remanence ratio of the 10 nm magnetic film is 0.82, which is much higher than the film remanence ratio of 0.46 at 50 nm. This is because when the thickness of the film is between 10 and 50 nm, the magnetic moments partially deviate from the in-plane direction, and the out-of-plane component reduces the film remanence ratio. This study shows that optimizing annealing temperature and film thickness can effectively control the structure and magnetic properties of Co magnetic films, which is of great significance for the development of the magnetic recording field.

Morphology and magnetic properties of Co0.8Fe2.2O4 films prepared by the chemical solution deposition

Soft Magnetism and Microwave Magnetic Properties of Fe-Co-Hf Films Deposited by Composition Gradient Sputtering

Magnetism of CoFe2O4 Thin Films Annealed under the Magnetic Field

Structure And Magnetic Properties Of Co2.73fe0.27o4 Synthesized By The Heat-Decomposition Method

Growth Temperature Dependent Evolutions of Microstructural, Optical and Magnetic Properties of Zn0.75Co0.25O Films

High-temperature Solid State Synthesis and Characterization in Magnetic and Transporting Properties of Zn_xFe_(3-x)O_4 Powder

Enhanced High-Frequency Electromagnetic Properties of FeCoB–SiO2/SiO2 Multilayered Granular Films

Microstructure, magnetic and magneto-optical properties of Co-Mn ferrite nanocrystalline films

Synthesis of CoFe2O4 Nanoparticles via Solution Method and Their Magnetic Properties

Structure and properties of Zn-doped CoFe 2 O 4 thin films via a sol–gel method

Magnetic Properties of Sputtered Fe1−xO and Fe+Fe3O4 Thin Films

Sol–gel Synthesis, Magnetic and Magneto-Optical Properties of CoFe2−xTbxO4 Nanocrystalline Films

Chemical Synthesis and Magnetic Study of Nanocrystalline Thin Films of Cobalt Spinel Ferrites

Magnetism and Phase Transition for CoFe2−xMnxO4 Nanocrystalline Thin Films and Powders

Structure and Performance Optimization of Co Magnetic Thin Films Deposited by Vacuum Evaporation Coating

Research on Double Resonance Peaks and Abnormal Frequency Shift in Permeability Spectra of Annealed FeCoB Films

Synthesis and influence of Zn substitution on optical and magnetic properties of cobalt ferrite nanoparticles by a polyacrylamide gel route

The Influence of Film Composition and Annealing Temperature on the Microstructure and Magnetic Properties of FeCo Thin Films

Investigation of Sm Addition on Microstructural and Optical Properties of CoFe Thin Films

Magnetic and Transport Properties of Zn0.4Fe2.6O4 Thin Films with Highly Preferential Orientation

Morphology, Microstructure and Magnetic Properties of Co2FeAl Alloy Nanostructures Prepared at Low Temperature