Abstract:This study has been proposed to increase the efficiency of the chemical loop process. Iron oxide doped with cobalt was used as a bifunctional material because of catalyst and oxygen carrier properties and methanol was used as a reducing agent. The co-precipitation method was used to synthesis of Co/Fe oxide. To evaluate the performance of the synthesized catalysts, a microchannel reactor was designed and built with a parallel channel arrangement. To increase H 2 /coke ratio, the effect of different amounts of cobalt (10, 20, and 30 %) in Fe 2 O 3 catalyst has been investigated. Then, the optimal amount of cobalt concentration was selected for investigation of reduction temperature from 350 to 450 °C. The results showed that increasing the Co concentration to 30 % and increasing the temperature of the reduction step to 450 °C causes the catalytic reactions to start in a shorter time and the process efficiency increases due to the high H 2 /coke ratio. The repeated cycles investigation of the 0.3CoFe 2 O 4 during 10 redox cycles showed decreased oxidation power and low stability. To enhance the oxidation power and stability, applying two-step reoxidation and adding Zr (30, 40 and 50 %) in the catalyst structure were examined. In the next step, using optimized Zr content (40%), to achieve pure H 2 stream for fuel cell applications, the reaction time of the reduction step was optimized. The results showed that during reduction times of 7 min, coke formation was prevented and pure H 2 (99.9999%) was produced. Finally, the stability of the 0.3CoFe 2 O 4 -ZrO 2 during 50 redox cycles in reduction time of 7 min showed that the use of Zr maintains the stability of the catalyst.

Carbon Monoxide-Free Hydrogen Production Via Low-Temperature Steam Reforming of Ethanol over Iron-Promoted Rh Catalyst

Low-temperature Catalytic Steam Reforming of Phenol for Hydrogen Production

Oxide-supported Rh Catalysts for H2 Generation from Low-Temperature Ethanol Steam Reforming: Effects of Support, Rh Precursor and Rh Loading on Catalytic Performance

Steam reforming of ethanol by non-noble metal catalysts

Highly efficient and stable photothermal catalytic CO<sub>2</sub> hydrogenation to methanol over Ru/In<sub>2</sub>O<sub>3</sub> under atmospheric pressure

Producing hydrogen by catalytic steam reforming of methanol using non-noble metal catalysts

Molecular Catalysis for the Steam Reforming of Ethanol

Non-syngas Direct Steam Reforming of Methanol to Hydrogen and Carbon Dioxide at Low Temperature

Ethanol Steam Reforming on Rh Catalysts: Theoretical and Experimental Understanding

Hydrogen Production from Steam Reforming of Ethanol over Pd Promoted ZnO/Al2O3 Catalysts

Bimetallic Fe‐Promoted Catalyst for CO‐Free Hydrogen Production in High‐Temperature‐Methanol Steam Reforming

Highly selective PdZn/ZnO catalysts for the methanol steam reforming reaction

Methanol Synthesis at a Wide Range of H 2 /CO 2 Ratios over a Rh‐In Bimetallic Catalyst

Development in Catalytic Systems in Hydrogen Production via Ethanol Steam Reforming

Photo-Assisted Catalytic CO 2 Hydrogenation to CO with Nearly 100% Selectivity over Rh/TiO 2 Catalysts

CO Hydrogenation over Fe-promoted Rh–Mn–Li/SiO2 Catalyst: the Effect of Sequences for Introducing the Fe Promoter

Production of clean hydrogen fuel on a bifunctional iron catalyst via chemical loop reforming of methanol

Iron-promoted zirconia-alumina supported Ni catalyst for highly efficient and cost-effective hydrogen production via dry reforming of methane

CO2 hydrogenation to methanol over Rh/In2O3 catalyst

Renewable Energy from Nature-Hydrogen Production from Bio-ethanol Steam Reforming

Hydrogen Production by Steam Reforming of Ethanol over CuO-La_2O_3/ZrO_2 Catalyst