Abstract:With the increasing severity in the service environment of secondary refining furnaces, traditional refractories cannot meet the high requirements. MgO-based fired refractories are subject to the thermal shock effect and slag penetration which are detrimental to their performance. In this study, low-carbon MgO-based refractories are reinforced by an in-situ MgAl2O4(MA)-TiO2 dense layer with the addition of low-cost self-prepared titanium carbonitride [Ti(C, N)]. The influence of the addition of as-prepared Ti(C, N) on the properties of low-carbon MgO-based refractories was investigated. The reinforced refractories had no cracks after 190 thermal shock cycles, demonstrating the highest hot modulus of rupture (HMOR) with excellent thermal shock resistance (TSR). After 2.5 h of rotary immersion in a steel slag, the corrosion depth of the composites was only 26.3% of that of commercial MgO-CaO refractories. Based on the thermodynamic analysis, the Ti(C, N) reinforcement mechanism for the low-carbon MgO-based refractories was studied. A MA-TiO2 dense layer formed during the oxidation process of the composites which enhanced the oxidation resistance. The volume expansion caused by the partial oxidation of Ti(C, N) prevents the penetration of the molten slag to refractories and Ti(C, N) powders forming a protective layer to further effectively protect the composites from slag corrosion owing to its high surface area. In addition, 3CaO·2TiO2 formed by the reaction between the steel slag and Ti(C, N) further increased the slag corrosion resistance (SCR) of the composites. This research offers a new idea for the material selection for secondary refining furnaces to achieve a green and effective steel-making production route and enriches the understanding of the phase behaviour in the Mg-Al-Ti-C-O-N system under high temperatures.

Improved Middle-Temperature Strength of Unfired Slide Gate Plate for Continuous Casting of Steel

Mechanical Properties and Thermal Stability of Carbide Dispersion Strengthened CLF-1 Steel

Failure analysis of Al2O3-C-SiO2 slide gate plates during continuous casting based on numerical simulation

Mechanical properties and microstructure evolution of MgO–Al–C slide plate refractories in presence of Al powder-modified magnesia aggregates

Investigation on a postmortem Al-Al2O3-fused mullite-containing Ti2O3 sliding gate

Properties and microstructure evolution of unfired Al–Si incorporated Al2O3–C slide plate materials with trace nano-Al2O3 particles

Evolution of iron-based raw materials and their effect on the properties of MgO-Al-C slide plate materials

Effect Of Alumina-Based Fiber On The Mid-Temperature Strength Of Integral Ceramic Mold For Casting Hollow Turbine Blade

Effect of pretreated Al-Si alloy powder on the microstructure and properties of Al 2 O 3 -SiC-C castables for iron runner

The influence of nanoparticles and functional metallic additions on the thermal shock resistance of carbon bonded alumina refractories

Corrosion mechanism of reactive MgO‐bonded Cr2O3‐bearing castables in CaO–Al2O3–Fe2O3–SiO2‐based steel‐making slag

Microstructure evolution, mechanical characteristics and erosion behavior of Cr2O3–Al2O3–MgO–ZrO2 refractories in molten reduction slag

Gelcasting of Alumina-Spinel Refractories

Significant improvement of slag corrosion resistance and thermal shock resistance of corundum‐based dry vibratable refractory by addition of Fe–Si 3 N 4

Microstructural evolution and properties enhancement of SiC refractory castables bonded with the special CNFs/calcium aluminate cement

Slag Corrosion Resistance of Al2O3-ZrN-Sialon-C Refractories

Improved properties of in-situ MgAl2O4-TiO2 dense layer reinforced low-carbon MgO-based refractories

Effects of Silica Sol/Phenolic Resin on Properties of Unfired Al2O3-β-Sialon/Ti(C,N)/SiC-C Composite Refractory Material

Microstructure and mechanical properties of CaAl12O19 reinforced Al2O3-Cr2O3 composites

Rheological and mechanical properties of aluminosilicious cementitious materials as refractory castable binders

Effect of Silicon Addition on Mechanical Properties of Mullite-Sic Composite Refractories