Abstract:Al2O3-SiC-C (ASC) castables containing spherical asphalt are widely utilized in high-temperature metallurgical furnaces because of their good abrasive resistance and slag resistance; however, the release of hazardous benzopyrene during the pyrosis process in spherical asphalt is detrimental to the environment and to the health of furnace workers. Herein, nontoxic nano carbon black (CB) was selected as the carbon source for ASC castables, and the effects of the CB amount and sintering atmosphere on the properties of ASC castables were investigated in this work. The results show that on increasing CB from 0.5% to 2%, the cold strength of the samples after firing in the reducing atmosphere increased, the residual strength increased, and the slag penetrated depth decreased; the reasons can be ascribed to nano CB being able to fill the pores to reduce the apparent porosity of the castables. Furthermore, SiC whiskers were formed at elevated temperatures and generated a network structure, which was beneficial in improving their properties. When CB was 1%, the cold modulus of the rupture of the samples after firing in the oxidizing atmosphere and reducing atmosphere were higher (about 20 MPa), the retained strength ratio of the samples pre-fired in the reducing atmosphere was the highest (85.4%), the hot strength at 1400 °C of the samples tested in the oxidized atmosphere was the highest (5.3 MPa), and the slag resistance of the samples measured in the oxidizing atmosphere was the best. The castables heat-treated in the air atmosphere possessed higher hot strength and slag resistance; the reasons can be attributed to the formed SiO2 derived from the oxidation of SiC, which reacted with Al2O3 to form mullite, creating a strengthening effect and decreasing the porosity and increasing the viscosity of slag, thereby improving the hot strength and slag resistance.

Effect of pretreated Al-Si alloy powder on the microstructure and properties of Al 2 O 3 -SiC-C castables for iron runner

Effect of Carbon Black Content and Firing Atmosphere on the Properties and Microstructure of Al2O3-SiC-C Castables

Effect of Al2O3 on the Molten Slag Microstructure Information by Molecular Dynamics Simulation and Experimental Analysis

Improving the anti-oxidation and water wettability of graphite through the design of coating structure for the preparation of Al2O3–SiC–C castables

Effect of modified coal tar pitch addition on the microstructure and properties of Al2O3–SiC–C castables for solid waste incinerators

The effect of microsilica on the oxidation resistance of Al2O3–SiC–SiO2–C castables with Si and B4C additives

Effects of different carbon-containing calcium aluminate cements on the microstructure and properties of Al2O3–SiC–C castables

Enhancing mechanism of improved slag resistance of Al2O3-spinel castables added with pre-synthesized (Al,Cr)2O3 micro-powder

Effects of Sintering Additives on Microstructure and Properties of Porous SiC Ceramics with High Porosity

Effect of silicon powder-modified tabular alumina aggregates on the mechanical properties and microstructures of carbon-bonded alumina refractories

The Effect of SiC on the Phase Composition and Structure of Mixed Slag

Properties and microstructure evolution of unfired Al–Si incorporated Al2O3–C slide plate materials with trace nano-Al2O3 particles

Microstructure and enhanced slag resistance of Al2O3–SiC–C refractory castables with addition of ammonium metatungstate

EFFECT OF AL(2)O(3) AND SIC CONTENT IN PACK CEMENTATION POWDERS ON THE MICROSTRUCTURE OF SIC COATINGS ON HTR GRAPHITE SPHERES

Improved Corrosion Resistance of Al2O3-SiC-C Castables Due to in Situ Synthesized TiC/TiN

Effect of SiC content on slag resistance of magnesia based castables

Sintering properties and microstructure of Al2O3-TiO2-CaO composite materials based on ferrotitanium slag

Preparation and properties of alumina-carbon castables using SiC nanofiber coated graphite flake

Effect of carbon black on corrosion resistance of Al2O3–SiC–C castables to SiO2–MgO slag

Restructuring-diffusion mechanism of calcium alumino-titanate in CaAl12O19–MgAl2O4–Al2O3 castables

Phase stability and enhanced mechanical properties of ferro-titanium slag to aluminum titanate ceramics