Preparations and Characterizations of New Mesoporous ZrO2 and Y2O3-stabilized ZrO2 Spherical Powders
Hui Zhang,Hu Lu,Yawei Zhu,Fan Li,Renguan Duan,Mei Zhang,Xidong Wang
DOI: https://doi.org/10.1016/j.powtec.2012.02.007
IF: 5.64
2012-01-01
Powder Technology
Abstract:In the absence of template and thermal stabilizer, novel mesoporous ZrO2 and Y2O3-stabilized ZrO2 (YSZ) spherical powders were synthesized via the improved spray reaction (SR) technique. The synthesized materials were characterized by thermo-gravimetry/differential thermal analysis (TG/DTA), scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), and Nitrogen adsorption/desorption isotherm techniques. Results reveal that the microstructure of ZrO2 precursor significantly depends on the aging process, and the particle size, surface area and phase composition of prepared ZrO2-based materials significantly depend on the calcination temperature. For pure ZrO2 spherical particles, the size varies from 1.63μm, 1.58μm to 1.60μm in correspondent to the calcined temperature 700°C, 800°C and 1000°C, respectively. And also the major cubic ZrO2 (c-ZrO2) is formed when calcined at 700°C whereas the predominant monoclinic ZrO2 (m-ZrO2) is synthesized when calcined at 800–1000°C. For YSZ spherical particles, the size changes from 1.65μm, 1.59μm, 1.62μm to 1.45μm in correspondent to the calcined temperature 500°C, 600°C, 700°C and 1000°C, respectively. The synthesized YSZ spheres exhibit the similar phase constitution of predominant tetragonal ZrO2 (t-ZrO2) at all experimental temperatures but show the different surface area and pore diameter, ~14.72m2/g surface area and 10.7nm pore diameter at 500°C as well as ~34.39m2/g surface area and 8.3nm pore diameter at 600°C.