Cobalt-free gadolinium-doped perovskite Gd x Ba 1 -x FeO 3 -δ as high-performance materials for oxygen separation

yanjie wang,qing liao,yan chen,libin zhuang,haihui wang

DOI: https://doi.org/10.1016/j.cjche.2015.08.023

IF: 3.8

2015-01-01

Chinese Journal of Chemical Engineering

Abstract:Cobalt-free oxides GdxBa1−xFeO3−δ (0.01≤x≤0.1) were achieved by a solid state reaction method. It is found that GdxBa1−xFeO3−δ (0.025≤x≤0.1) exhibits the cubic perovskite structure. Among GdxBa1−xFeO3−δ (0.025≤x≤0.1), the Gd0.025Ba0.975FeO3−δ (GBF2.5) membrane shows the outstanding phase structure stability and the highest oxygen permeation, which can reach 1.44ml·cm−2·min−1 at 950°C under air/He oxygen partial pressure gradient. The GBF2.5 membrane was successfully operated for more than 100h at 800°C and the oxygen permeation flux through the membrane is 0.62ml·cm−2·min−1. After 100h oxygen permeation experiment at 800°C, X-ray diffraction (XRD) and energy dispersive X-ray spectrometer (EDXS) demonstrate that the GBF2.5 exhibits phase structure stability even at intermediate temperature.