Abstract:Carbon fiber reinforced silicon carbide matrix composites have received considerable attention because of their superior friction behavior. In this paper, carbon/silicon carbide composites were fabricated by chemical vapor infiltration. The microstructure, mechanical properties, and the friction behavior were investigated. The carbon fiber preform was fabricated with the three dimension needling method, and the infiltrated carbon/silicon carbide (C/SiC) composites exhibited excellent shear strength. The in-plane shear strength and the inter-laminar shear strength are 85 and 27MPa, respectively. The composites show non-brittle failure behavior resulting from fiber pull-out as well as fiber cluster pull-out. The friction behavior and friction stability are significantly improved by increasing both the density and carbon content of the composites. If the density of the composite is 2.3gcm−3, the coefficient of friction measured is 0.23, the coefficient of friction stability (as it will be defined later on) is 0.43, and the liner wear rate is less than 9.3μm/cycle. Moreover, the C/SiC composites demonstrate a good friction property against fading versus several braking stops. The rapid increase of friction coefficient approaching the end of braking is mainly related to the increasing of surface temperature in a short time and the enhanced adhesion and abrasion of contact conjunctions and asperities. The friction surface is covered with wear debris including flake materials and fragments of carbon fiber. The micro-cracks and grooves observed on the friction surface are significantly determined by cyclic mechanical and thermal stresses.

The mechanical properties and thermal conductivity of carbon/carbon composites with the fiber/matrix interface modified by silicon carbide nanofibers

Mechanical Properties of Carbon/carbon Composites with the Fibre/matrix Interface Modified by Carbon Nanofibers

Thermal Conductivity of Carbon/Carbon Composites with the Fiber/Matrix Interface Modified by Silicon Carbide Nanofibers

Mechanical Behavior of SiCf/SiC Composites with Alternating PyC/SiC Multilayer Interphases

Properties of Carbon Nano-Tubes–cf/sic Composite by Precursor Infiltration and Pyrolysis Process

The Mechanical Property of C/C Composites Modified by SiCNF

Friction and Wear Behaviors of SiCNF Modified Carbon/carbon Sealing Materials

The Improvement of Mechanical Properties of SiC/SiC Composites by in Situ Introducing Vertically Aligned Carbon Nanotubes on the PyC Interface

The Improvement in the Mechanical and Thermal Properties of SiC/SiC Composites by Introducing CNTs into the PyC Interface

Mechanical properties and fracture behavior of CVI-SiC/TaC modified C/C composite

INFLUENCE OF MATRIX MODIFICATION ON MICROSTRUCTURE AND PROPERTIES OF CARBON FIBER REINFORCED SILICON CARBIDE COMPOSITES

Mechanical properties of C/C-SiC composites by compression molding

Enhanced thermal and mechanical properties of optimized SiC<sub><i>f</i></sub>/SiC composites with in-situ CNTs on PyC interface

Enhanced Thermal and Mechanical Properties of Optimized SiCf/SiC

Effect of Pyrocarbon Content in C/C Preforms on Microstructure and Mechanical Properties of the C/C–SiC Composites

Microstructure and mechanical property of short fiber reinforced C/C-SiC composites

Preparation and Friction Behavior of Carbon Fiber Reinforced Silicon Carbide Matrix Composites

Carbon Fiber Surface Nano-Modification and Enhanced Mechanical Properties of Fiber Reinforced Cementitious Composites

3C-SiC Nanowires In-Situ Modified Carbon/Carbon Composites and Their Effect on Mechanical and Thermal Properties

Fabrication of SiCf/SiO2 Composites and the Influence of Interfaces on the Mechanical Properties

Microstructures and Mechanical Properties of Three-Dimensional Ceramic Filler Modified Carbon/carbon Composites