Abstract:The brazing of C/C and C f /SiC composites was achieved using Si–14Ti eutectic filler. The wetting behavior of the Si–Ti filler on the composites, as well as the microstructure and performance of the joints at different brazing temperatures, were characterized. The results showed that the contact angle of Si–Ti eutectic filler on precursor infiltration and pyrolysis (PIP)-C f /SiC composite surface is only 60°, while it exhibits good spreading effect on liquid silicon infiltration (LSI)-C f /SiC and C/C composite surfaces. Although Si–Ti filler and carbon fiber reinforced composites (C/C, PIP-C f /SiC and LSI-C f /SiC) react to form SiC, the joint shows different mechanical performance. The liquid filler infiltrates into the gaps between fiber bundles and reacts with C/C to form a SiC reaction layer at the interface. However, the presence of numerous defects at the brazed joint between Si–Ti filler and PIP-C f /SiC results in the shear strength of only 28 MPa for the C/C-PIP-C f /SiC joint. While for the C/C-LSI-C f /SiC joint, due to the residual Si in the LSI-C f /SiC composites, the liquid filler infiltrates intensely into LSI-C f /SiC to form a unique C f /SiC–Si–TiSi 2 compound infiltration layer. The shear strength of C/C-LSI-C f /SiC joints reaches 47 MPa, with fracture occurring in both substrates and brazed seam. The present study offers theoretical support for the investigation of Si-based fillers in brazing carbon fiber reinforced ceramic matrix composites.

Microstructures and Mechanical Properties of Three-Dimensional Ceramic Filler Modified Carbon/carbon Composites

Mechanical Behavior of SiCf/SiC Composites with Alternating PyC/SiC Multilayer Interphases

Mechanical Properties of 3D KD-I SiCf/SiC Composites with Engineered Fibre–matrix Interfaces

Preparation and mechanical behaviors of multiscale SiC nanowires/carbon fiber reinforced silicon oxycarbide ceramic composites

Microstructure and mechanical properties of 3D Cf/SiBCN composites fabricated by polymer infiltration and pyrolysis

Microstructure and mechanical property of Cf/SiC core/shell composite fabricated by direct ink writing

Microstructure and properties of different carbon fiber reinforced ceramic composites brazed joint by Si-Ti alloy filler

Microstructure Characterization by X-Ray Computed Tomography of C/C-SiC Ceramic Composites Fabricated with Different Carbon Fiber Architectures

Mechanical Properties and Failure Behavior of 3D-SiCf/SiC Composites with Different Interphases

Fabrication and characterization of carbon fiber reinforced SiC ceramic matrix composites based on 3D printing technology

Microstructure and mechanical properties of SiC f /SiC composite prepared by chemical vapor infiltration

Characterization of the Microstructure of Three‐Dimensional‐Needled Carbon/Silicon Carbide Composites

Microstructure and Mechanical Properties of Unidirectional, Laminated Cf/SiC Composites with α-Al2O3 Nanoparticles as Filler

Fabrication of dense Cf/SiC ceramic matrix composites using 3D printing and PIP with short carbon fibre as a toughening material

Microstructures and properties of C/C–SiC composites derived from different gaseous carbon matrix precursors

Microstructure and Mechanical Properties of C/C Composites Modified by Single-Source Precursor Derived Ceramics

Effects of preform structure on microstructure and mechanical properties of long/short fiber‐coupled C/C–SiC composites

Preparation, microstructure and properties of three-dimensional carbon/carbon composites withhigh thermal conductivity

Fabrication and microstructure evolution of Csf/ZrB2-SiC composites via direct ink writing and reactive melt infiltration

Architectural Engineering Inspired Method of Preparing C-f/ZrC-SiC with Graceful Mechanical Responses

Mechanical and ablation properties of 3D orthogonal woven C/C-SiC composite based on high-solid-loading slurry impregnation