Abstract:The hydrolysis of an industrial titanyl sulfate (TiOSO4) solution to metatitanic acid (H2TiO3) is the crucial step in the production of titanium dioxide (TiO2) using the sulfuric acid process, and the extra-adding seeded route is generally adopted in industry, in which the quality of the crystal seeds plays a critical role. In this study, the optimal process conditions for preparing the crystal seeds via the NaOH neutralization method were first investigated. Then, the ultrasound-assisted preparation of crystal seeds was studied to explore the effect of the ultrasonic time and intensity on the particle size and particle size distribution of crystal seeds. The results demonstrated that ultrasonic assistance is helpful in obtaining crystal seeds with smaller particle sizes and more uniform particle size distribution, and the quality of the hydrolysis product of H2TiO3, i.e., the particle size and its distribution, is strictly correlated with those of the crystal seeds. Under the optimal process conditions for preparing the hydrolytic seeds, the average particle of the hydrolytic seeds prepared without ultrasonic assistance is 25.50 nm. In contrast, the introduction of ultrasonic assistance in the preservation stage could significantly decrease the particle size and narrow the particle size distribution of the hydrolytic seeds. When the ultrasonic time is 4 min and the ultrasonic intensity is 40 W, the average particle of the hydrolytic seeds is decreased to 23.48 nm. Therefore, the quality of the crystal seeds, as well as that of H2TiO3 products, could be significantly improved by introducing ultrasonic assistance with a suitable intensity at a suitable time in the preparation process of crystal seeds via the NaOH neutralization method.

Ultrasound assisted salts–metal reaction for synthesizing TiB2 particles at low temperature

Low-temperature Synthesis of Nano-Sized TiC Particles by Ultrasound Assisted Melt-Reaction of Al-K2TiF6-C System

Low-temperature Synthesis of TiB2 Nanocrystals Using TiO2 ,LiBH4 and Mg

A Quantitative Study of the Synthesis of TiB2 Particles Via Salts-Metal Reaction at Different Temperatures

Low‐temperature Synthesis of Ultrafine TiB2 Nanopowders by Molten‐salt Assisted Borothermal Reduction

Ultrasound-induced Distribution of Nano-Sized TiB2 Particles Within Α-Al Grains During Solidification of Al-7Si Alloy

Synthesis of Ti0.2Zr0.8B2 Solid‐solution Nanopowders by Molten Salt Assisted Borothermal Reduction

Low-temperature synthesis of nanosized metal borides through reaction of lithium borohydride with metal hydroxides or oxides

Low-Temperature High-Efficiency Preparation of TiB 2 Micro-Platelets via Boro/Carbothermal Reduction in Microwave Heated Molten Salt.

Ultrasound Induced a More Homogeneous Distribution of TiB2 Particles in Al Matrix During Solidification

A convenient solid-state reaction route to nanocrystalline TiB2

Room-Temperature Synthesis of BaTiO<sub>3</sub>Nanoparticles in Large Batches

Low-temperature Synthesis of Bi4Ti3O12 Nanocrystals by Hydrothermal Method

Ultrasound Assisted Combustion Synthesis of TiC in Al–Ti–C System

Synthesis of Bi0.5(Na0.7K0.2Li0.1)0.5TiO3 powders through the molten salt method

Low-temperature synthesis of high-purity TiB2 via carbothermal reduction of metatitanic acid and H3BO3

In-situ Synthesis of Nanocrystalline TiC Powders, Nanorods, and Nanosheets in Molten Salt by Disproportionation Reaction of Ti(II) Species

Refinement of Tib2 in Al-Ti-B Grain Refiner Alloys by Ultrasound and the Effect on Al Grain Size

A New Method for Synthesizing Li2.06nb0.18ti0.76o3 Powder at Low Temperatures

The Ultrasound-Assisted Preparation of Crystal Seeds for the Hydrolysis of TiOSO4 to H2TiO3

Effects of Ultrasound Assisted Solidificaiton on the Microstructure and Mechanical Properties of Nano-Sized TiB2/Al-4.5Cu Composites