Microwave dielectric properties of low-fired Li 2 ZnTi 3 O 8 –TiO 2 composite ceramics with Li 2 WO 4 addition

Ying-Xiang Li,Hao Li,Bin Tang,Zhen-Jun Qin,He-Tuo Chen,Shu-Ren Zhang

DOI: https://doi.org/10.1007/s10854-014-2522-x

2014-01-01

Abstract:The effects of Li 2 WO 4 addition on phase composition, microstructure and dielectric properties of Li 2 ZnTi 3 O 8 –TiO 2 (LZT) composite ceramics have been investigated. It was found that a small amount of LW additives could effectively lower the sintering temperature of LZT ceramics from 1,160 to 860 °C without a serious degradation of the microwave dielectric properties. Dense Li 2 WO 4 -doped LZT samples of a relative sintered density over 96 % could be prepared even at 840 °C. With increasing Li 2 WO 4 addition up to 4 wt%, both of the ε r and τ f were slightly decreased, while the Q × f was increased firstly, then reached the maximum, and finally declined with the additive further increased. Typically, 2.0 wt% Li 2 WO 4 added LZT ceramic sintered at 860 °C for 4 h exhibited good microwave dielectric properties of ε r = 27.1, Q × f = 51,123 GHz and τ f = −3.8 ppm/°C, which made it promising for low temperature co-fired ceramics technology application.