Abstract:A series of V-Ce(SO4)(2)/Ti catalysts for selective catalytic reduction (SCR) of NO with ammonia are prepared by impregnation method. Low temperature SCR activity and alkali resistance of the optimal V-0.5Ce(SO4)(2)/Ti sample are found to be better than on the commercial V-W/Ti catalyst. Also, V-0.5Ce(SO4)(2)/Ti shows an excellent durability in the presence of SO2 and H2O, indicating to have prospects for the industrial application. Based on catalysts characterization and in-situ DRIFTS studies, a higher proportion of surface active oxygen generated by the introduction of Ce and a Much faster H-2 reduction point out the improved redox properties of V-0.5Ce(SO4)(2)/Ti, which results in a stronger NO oxidative activation and is confirmed by a more abundant formation of surface NO and NO3-species. When exposed to SCR conditions where both NH3 and NO are present, this enhanced NO activation can produce more reactive nitrite and/or NO+ intermediates which then readily react with adsorbed NH3 and decorripose to N-2 and H2O, accounting for the improved SCR activity of V-0.5Ce(SO4)(2)/Ti at low temperatures. The addition of Ce(SO4)(2) also provides abundant reactive acid sites and adsorbed NH3 species thus increase. Even after Na poisoning, adequate surface acidity and redox properties still remain. Furthermore, relatively higher contents of V-OH are preserved owing to the interaction between Na and O=S=O, acting as a protection for the active sites. These promotional effects contribute to the better alkali resistance of V-0.5Ce(SO4)(2)/Ti. Therefore, all the results suggest that V-0.5Ce(SO4)(2)/Ti is a promising candidate as a catalyst for NH3-SCR in coal-fired power plants, especially under high Na-content conditions. (C) 2017 Elsevier B.V. All rights reserved.

Ultra Hydrothermal Stability of CeO2-WO3/TiO2 for NH3-SCR of NO Compared to Traditional V2O5-WO3/TiO2 Catalyst

Ultra-high Hydrothermal Stability of Ce-based NH3-SCR Catalyst for Diesel Engines: A Substitute for Cu Zeolites

Low-temperature Activity and Mechanism of WO3-modified CeO2-TiO2 Catalyst under NH3-NO/NO2 SCR Conditions

Enhancement of the Hydrothermal Stability of WO3/Ce0.68Zr0.32O2 Catalyst by Silica Modification for NH3-SCR

Activity and Hydrothermal Stability of CeO_2–ZrO_2–WO_3 for the Selective Catalytic Reduction of NO_x with NH_3

Hydrothermal and Sulfur Aging of CeTi/CeWTi Catalysts for Selective Catalytic Reduction of NOx with NH3

Ceria-modified WO3-TiO2-SiO2 Monolithic Catalyst for High-Temperature NH3-SCR

Synergistic Effect Between Ceria and Tungsten Oxide on WO3–CeO2–TiO2 Catalysts for NH3-SCR Reaction

Introducing Tin to Develop Ternary Metal Oxides with Excellent Hydrothermal Stability for NH3 Selective Catalytic Reduction of NOx

A Comprehensive Study on Sulfur Tolerance of Niobia Modified CeO2/WO3-TiO2 Catalyst for Low-Temperature NH3-SCR

Improvement in Activity and Alkali Resistance of a Novel V-Ce(SO4)2/Ti Catalyst for Selective Catalytic Reduction of NO with NH3

Enhanced Durability of Monolithic V2O5-WO3/TiO2 Catalysts Prepared by a Novel One-Pot Method for the Selective Catalytic Reduction of NOx with NH3

Promotional Effect of H2O2 Modification on the Cerium-Tungsten-titanium Mixed Oxide Catalyst for Selective Catalytic Reduction of NO with NH3

Effects of WO3 and SiO2 Doping on CeO2–TiO2 Catalysts for Selective Catalytic Reduction of NO with Ammonia

DRIFT Study on Cerium−Tungsten/Titiania Catalyst for Selective Catalytic Reduction of NOx with NH3

Effect of Ce Doping of TiO2 Support on NH3-SCR Activity over V2O5–WO3/CeO2–TiO2 Catalyst

Enhanced activity of tungsten modified CeO2/TiO2 for selective catalytic reduction of NOx with ammonia

A Novel Nb-Ce/Wox-Tio2 Catalyst with High Nh3-Scr Activity and Stability

TiO2-modified CeVO4 catalyst for the selective catalytic reduction of NOx with NH3

Low-temperature SCR Activity and SO2 Deactivation Mechanism of Ce-modified V2O5–WO3/TiO2 Catalyst

A basic comprehensive study on synergetic effects among the metal oxides in CeO2-WO3/TiO2 NH3-SCR catalyst