Abstract:A series of V-Ce(SO4)(2)/Ti catalysts for selective catalytic reduction (SCR) of NO with ammonia are prepared by impregnation method. Low temperature SCR activity and alkali resistance of the optimal V-0.5Ce(SO4)(2)/Ti sample are found to be better than on the commercial V-W/Ti catalyst. Also, V-0.5Ce(SO4)(2)/Ti shows an excellent durability in the presence of SO2 and H2O, indicating to have prospects for the industrial application. Based on catalysts characterization and in-situ DRIFTS studies, a higher proportion of surface active oxygen generated by the introduction of Ce and a Much faster H-2 reduction point out the improved redox properties of V-0.5Ce(SO4)(2)/Ti, which results in a stronger NO oxidative activation and is confirmed by a more abundant formation of surface NO and NO3-species. When exposed to SCR conditions where both NH3 and NO are present, this enhanced NO activation can produce more reactive nitrite and/or NO+ intermediates which then readily react with adsorbed NH3 and decorripose to N-2 and H2O, accounting for the improved SCR activity of V-0.5Ce(SO4)(2)/Ti at low temperatures. The addition of Ce(SO4)(2) also provides abundant reactive acid sites and adsorbed NH3 species thus increase. Even after Na poisoning, adequate surface acidity and redox properties still remain. Furthermore, relatively higher contents of V-OH are preserved owing to the interaction between Na and O=S=O, acting as a protection for the active sites. These promotional effects contribute to the better alkali resistance of V-0.5Ce(SO4)(2)/Ti. Therefore, all the results suggest that V-0.5Ce(SO4)(2)/Ti is a promising candidate as a catalyst for NH3-SCR in coal-fired power plants, especially under high Na-content conditions. (C) 2017 Elsevier B.V. All rights reserved.

A Novel Nb-Ce/Wox-Tio2 Catalyst with High Nh3-Scr Activity and Stability

Ceria-modified WO3-TiO2-SiO2 Monolithic Catalyst for High-Temperature NH3-SCR

Ultra Hydrothermal Stability of CeO2-WO3/TiO2 for NH3-SCR of NO Compared to Traditional V2O5-WO3/TiO2 Catalyst

A Comprehensive Study on Sulfur Tolerance of Niobia Modified CeO2/WO3-TiO2 Catalyst for Low-Temperature NH3-SCR

Monolith Ce0.65zr0.35o2-Based Catalysts for Selective Catalytic Reduction of No with Nh3

A Superior Cerium-Tungsten Bimetal Oxide Catalyst with Flower-Like Structure for Selective Catalytic Reduction of NO by NH3

Ce and Zr Modified WO3-TiO2 Catalysts for Selective Catalytic Reduction of NOx by NH3

Low-temperature Activity and Mechanism of WO3-modified CeO2-TiO2 Catalyst under NH3-NO/NO2 SCR Conditions

Promotional Effect of Niobium Substitution on the Low-Temperature Activity of a WO3/CeZrOx Monolithic Catalyst for the Selective Catalytic Reduction of NOx with NH3

Activity and Hydrothermal Stability of CeO_2–ZrO_2–WO_3 for the Selective Catalytic Reduction of NO_x with NH_3

Effects of WOx Modification on the Activity, Adsorption and Redox Properties of CeO2 Catalyst for NOx Reduction with Ammonia

Design and Synthesis of Highly-Dispersed WO3 Catalyst with Highly Effective NH3-SCR Activity for NOX Abatement

Enhanced activity of tungsten modified CeO2/TiO2 for selective catalytic reduction of NOx with ammonia

Three-dimensionally ordered macroporous Ce-W-Nb oxide catalysts for selective catalytic reduction of NO with NH3

CeO 2 –WO 3 Mixed Oxides for the Selective Catalytic Reduction of NO X by NH 3 over a Wide Temperature Range

CuOx and WOx modified CeO2-TiO2 with various morphologies for the selective catalytic reduction of NOx with NH3

Excellent low-temperature NH3-SCR of NO activity and resistance to H2O and SO2 over WaCeOx (a=0.06, 0.12, 0.18, 0.24) catalysts: Key role of acidity derived from tungsten addition

Improvement in Activity and Alkali Resistance of a Novel V-Ce(SO4)2/Ti Catalyst for Selective Catalytic Reduction of NO with NH3

Novel Promoting Effects of Cerium on the Activities of NOx Reduction by NH3 over TiO2-SiO2-WO3 Monolith Catalysts

CeO2-WO3 catalysts for the selective catalytic reduction of NOx with NH3: effect of the amount of WO3

Abatement of Nitrogen Oxides Via Selective Catalytic Reduction over Ce1-W1 Atom-Pair Sites.