Abstract:A series of V-Ce(SO4)(2)/Ti catalysts for selective catalytic reduction (SCR) of NO with ammonia are prepared by impregnation method. Low temperature SCR activity and alkali resistance of the optimal V-0.5Ce(SO4)(2)/Ti sample are found to be better than on the commercial V-W/Ti catalyst. Also, V-0.5Ce(SO4)(2)/Ti shows an excellent durability in the presence of SO2 and H2O, indicating to have prospects for the industrial application. Based on catalysts characterization and in-situ DRIFTS studies, a higher proportion of surface active oxygen generated by the introduction of Ce and a Much faster H-2 reduction point out the improved redox properties of V-0.5Ce(SO4)(2)/Ti, which results in a stronger NO oxidative activation and is confirmed by a more abundant formation of surface NO and NO3-species. When exposed to SCR conditions where both NH3 and NO are present, this enhanced NO activation can produce more reactive nitrite and/or NO+ intermediates which then readily react with adsorbed NH3 and decorripose to N-2 and H2O, accounting for the improved SCR activity of V-0.5Ce(SO4)(2)/Ti at low temperatures. The addition of Ce(SO4)(2) also provides abundant reactive acid sites and adsorbed NH3 species thus increase. Even after Na poisoning, adequate surface acidity and redox properties still remain. Furthermore, relatively higher contents of V-OH are preserved owing to the interaction between Na and O=S=O, acting as a protection for the active sites. These promotional effects contribute to the better alkali resistance of V-0.5Ce(SO4)(2)/Ti. Therefore, all the results suggest that V-0.5Ce(SO4)(2)/Ti is a promising candidate as a catalyst for NH3-SCR in coal-fired power plants, especially under high Na-content conditions. (C) 2017 Elsevier B.V. All rights reserved.

Low-temperature SCR Activity and SO2 Deactivation Mechanism of Ce-modified V2O5–WO3/TiO2 Catalyst

Low-temperature Activity and Mechanism of WO3-modified CeO2-TiO2 Catalyst under NH3-NO/NO2 SCR Conditions

Promotional Effect of Ce-doped V<sub>2</sub>O<sub>5</sub>-WO<sub>3</sub>/TiO<sub>2</sub>with Low Vanadium Loadings for Selective Catalytic Reduction of NO<i><sub>x</sub></i>by NH<sub>3</sub>

New Insight into SO2 Poisoning and Regeneration of CeO2-WO3/TiO2 and V2O5-WO3/TiO2 Catalysts for Low-Temperature NH3-SCR

The role of cerium in the improved SO2 tolerance for NO reduction with NH3 over Mn-Ce/TiO2 catalyst at low temperature

Promotional effect of CeO2 on low-temperature selective catalytic reduction of NO by NH3 over V 2 O5-WO3/TiO2 catalysts

Improvement in Activity and Alkali Resistance of a Novel V-Ce(SO4)2/Ti Catalyst for Selective Catalytic Reduction of NO with NH3

Temperature sensitivity of the selective catalytic reduction (SCR) performance of Ce-TiO2 in the presence of SO2

Abatement of Nitrogen Oxides Via Selective Catalytic Reduction over Ce1-W1 Atom-Pair Sites.

Ceria accelerates ammonium bisulfate decomposition for improved SO2 resistance on a V2O5-WO3/TiO2 catalyst in low-temperature NH3-SCR

Ultra Hydrothermal Stability of CeO2-WO3/TiO2 for NH3-SCR of NO Compared to Traditional V2O5-WO3/TiO2 Catalyst

The Effect of CeO2 on the Catalytic Activity and SO2 Resistance of the V2O5-MoO3/TiO2 Catalyst Prepared Using the Ball Milling Method for the NH3-SCR of NO

Enhancement of activity and sulfur resistance of CeO2 supported on TiO2-SiO2 for the selective catalytic reduction of NO by NH3

Abatement of Nitrogen Oxides via Selective Catalytic Reduction over Ce 1 –W 1 Atom-Pair Sites

Effects of WO3 and SiO2 Doping on CeO2–TiO2 Catalysts for Selective Catalytic Reduction of NO with Ammonia

TiO2-modified CeVO4 catalyst for the selective catalytic reduction of NOx with NH3

Effect of Synthesis Methods on Activity of V2O5/CeO2/WO3-TiO2 Catalyst for Selective Catalytic Reduction of NOx with NH3

Effect of SiO2 addition on NH4HSO4 decomposition and SO2 poisoning over V2O5-MoO3/TiO2-CeO2 catalyst

Effects of Cerium and Vanadium on the Activity and Selectivity of MnOx-TiO2 Catalyst for Low-Temperature NH3-SCR

Highly Efficient Mesoporous V2O5/WO3–TiO2 Catalyst for Selective Catalytic Reduction of NOx: Effect of the Valence of V on the Catalytic Performance

VxMn(4-x)Mo3Ce3/Ti catalysts for selective catalytic reduction of NO by NH3