Water-stable Lithium Ion Conducting Solid Electrolyte of the Li1.4Al0.4Ti1.6−xGex(PO4)3 System (x=0–1.0) with NASICON-type Structure

Peng Zhang,Masaki Matsui,Atsushi Hirano,Yasuo Takeda,Osamu Yamamoto,Nobuyuki Imanishi

DOI: https://doi.org/10.1016/j.ssi.2013.09.022

IF: 3.699

2013-01-01

Solid State Ionics

Abstract:Solid ionic conductors composed of Li1.4Al0.4Ti1.6−xGex(PO4)3 (x=0–1.0) with the NASICON-type structure were synthesized with a precursor prepared using the sol–gel method. The electrical conductivity was examined as a function of x in Li1.4Al0.4Ti1.6−xGex(PO4)3 at various sintering temperatures and for various sintering periods. The highest electrical conductivity was obtained for Li1.4Al0.4Ti1.4Ge0.2(PO4)3 sintered at 900°C for 11h in air. The total and bulk conductivities of the sintered pellet were 1.29×10−3 and 2.35×10−3Scm−1 at 25°C, respectively. The grain boundary resistance of Li1.4Al0.4Ti1.4Ge0.2(PO4)3 was significantly increased to 552Ωcm2 from 12.2Ωcm2 by immersion in distilled water at 50°C for one week, whereas the bulk resistance was not increased. However, no significant increase of the bulk and grain boundary resistance was observed after immersion in a saturated aqueous solution of LiOH and LiCl.