Structure transitions of lithium ionic conductor Li2PS4
Jianing Liang,Xiaowei Xu,Cheng Zeng,Shuhao Wang,Haoyue Liang,Huiqiao Li
DOI: https://doi.org/10.1360/TB-2021-1027
2022-01-01
Abstract:Traditional lithium-ion batteries have a low energy density and pose safety risks due to the use of graphite-based anode materials and combustible organic liquid electrolytes. Advanced next-generation battery devices are urgently needed to store more energy and be used more safely in emerging and existing technologies such as electric vehicles and distributed energy storage. All-solid-state batteries made up of high-voltage cathodes and lithium metal anodes are promising candidates for achieving high safety and competitive energy power density. The nonflammable solid electrolytes (SEs) are key components that separate cathode and anode, migrate lithium ions. and support the cell framework. Among different types of SEs, thiophosphates Li3PS4, as a thio-LISICON (lithium superionic conductor), have attracted considerable interest of researchers as inorganic SEs due to their superior room-temperature ionic conductivities, desirable mechanical properties, and compliant chemical compatibility. According to the arrangement mode of PS43- tetrahedron, Li3PS4 possesses different polymorph structures (glass-, alpha-, beta-, and gamma-Li3PS4), which play a critical role in ionic conductivity because of the strong dependence on ionic conductivity and crystalline phases. Under heat treatment conditions, polymorphs can transform into each other. Thus, investigating the synthesis conditions and phase transitions between different crystal structures is of great significance for the application of SEs. Ball-milling combined with a heat-sintering process is used to create different-structured Li3PS4. In situ variable temperature Raman and room-temperature X-ray diffraction are used to delineate the transitions between different phases. focusing on investigating the transition conditions among different crystal structures and the relationship between the structures and ionic conductivity. Glass-Li3PS4 can be easily obtained by ball-milling Li2S and P2S5 powders and preferentially transformed into the metastable beta-phase when the sintering temperature is raised to 240 degrees C. which can retain the beta-Li3PS4 structure and show high ionic conductivity (0.65 mS cm(-1)) after cooling to room temperature. Once at a higher sintering temperature (>480 degrees C), the beta-phase will then transform into the super-higher ionic conductivity but thermodynamically unstable alpha-phase. More interesting, the alpha-phase would directly transform into a thermodynamically stable gamma-phase without the appearance of beta-phase during the subsequent cooling process, while the gamma-phase is not a favorable structure for Li-ions migration due to its low ionic conductivity (0.004 mS cm(-1)). Furthermore, we discuss some potential strategies for lowering the phase transition temperature to obtain alpha-Li3PS4 superconductors at room temperature (e.g.. generation of pinning effect from element doping to restrict the movement and rearrangement of PS43- tetrahedron, use of the high surface-area framework to stabilize the high-temperature structure, and the quenching process). Moreover, gamma-phase and alpha-phase Li3PS4 show a certain fabric memory' effect, which enables them to retain their inherent structure even after resintering at 240 degrees C. The results reveal that the thermodynamically metastable beta-Li3PS4 can be easily obtained at room temperature by precisely controlling the sintering temperature; there is no need for an assisted route such as forming nanoporous using solvent-assisted route or substituting cationic to obtain "beta-like" phase. Finally, the Li-Li symmetric batteries assembled from different structural Li3PS4 phases show that the beta-Li3PS4 provides better interfacial stability, which may meet the demands of SEs in solid-state batteries.