Y2o3-Modified Ba(Ti0.96sn0.04)O-3 Ceramics with Improved Piezoelectricity and Raised Curie Temperature

Mingli Chen,Zhijun Xu,Ruiqing Chu,Zhe Wang,Shasha Gao,Guohao Yu,Wei Li,Shuwen Gong,Guorong Li

DOI: https://doi.org/10.1016/j.materresbull.2014.07.040

IF: 5.6

2014-01-01

Materials Research Bulletin

Abstract:Ba(Ti0.96Sn0.04)O-3-xY(2)O(3) (BTS-Y) lead-free piezoceramics are fabricated by the conventional solid state reaction technique. The influences of Y3+ substitution on the phase structure, dielectric properties and piezoelectricity of BTS-Ypiezoceramics are investigated. XRD patterns show the ceramics possess a pure perovskite structure. The orthorhombic-tetragonal (O-T) phase transition dielectric peak shifts toward lower temperature with increasing Y3+ content The compositions x = 0.15-0.25% that are at O-T polymorphic phase transition region possess excellent piezoelectricity and the maximum piezoelectric constant d(33) of 454pC/N is obtained at x = 0.2%. The ceramics' Curie temperatures (T-c) are monotonically increased from 71 degrees C for x = 0-86 degrees C for x = 0.4% due to Y3+ substitution and the usage temperature range of BTS-Y piezoceramics is broadened. Compared with Ca2+ which also decreases the O-T phase transition temperature (TO-T) but hardly affects the T-c of BaTiO3-based ceramics, Y3+ substitution seems to be more beneficial for the practical application of the piezoceramics. (C) 2014 Elsevier Ltd. All rights reserved.