Enhancement of the temperature stabilities in yttrium doped (Ba 0.99Ca 0.01)(Ti 0.98Zr 0.02)O 3 ceramics

Wei Li,Jigong Hao,Wangfeng Bai,Zhijun Xu,Ruiqing Chu,Jiwei Zhai

DOI: https://doi.org/10.1016/j.jallcom.2012.03.110

IF: 6.2

2012-01-01

Journal of Alloys and Compounds

Abstract:Lead-free (Ba 0.99Ca 0.01)(Ti 0.98Zr 0.02)O 3 + x mol% (x = 0-0.8) Yttrium ceramics (BCZT-Y) were prepared using the solid-state reaction technique. High piezoelectric coefficient of d 33 = 360 pC/N and planar electromechanical coupling factor of k p = 42% were obtained at x = 0.2. Furthermore, greatly enhanced temperature stabilities of the piezoelectric properties were obtained in the temperature range from 20 to 100 °C, in which the BCZT-Y ceramics exhibited pure tetragonal phase. With the increase of Yttrium content, the orthorhombic-tetragonal phase transition shifted toward low temperature, while Curie temperature (T C) maintained at about 120 °C. The results indicate that the BCZT-Y ceramics are promising lead-free materials for practical applications. © 2012 Elsevier B.V. All rights reserved.