Abstract:The continuous development of lithium -ion batteries (LIBs) manufacturing industry calls for the mass production of Li 2 CO 3 , which serves as a pivotal raw material for LIBs. In our previous study, Li was successfully precipitated as intermediate product Li 2 SiO 3 from an alkaline solution containing Si by the hydrothermal precipitation method, realizing the preliminary separation of Li and impurities. In this research, H 2 SO 4 digestion -water leaching-Na 2 CO 3 precipitation process was proposed to manufacture Li 2 CO 3 from the intermediate product Li 2 SiO 3 . Firstly, the reaction feasibility of H 2 SO 4 digestion -water leaching and direct H 2 SO 4 leaching for Li 2 SiO 3 were comparatively evaluated through thermodynamic calculation and experimental research. Compared to direct H 2 SO 4 leaching, H 2 SO 4 digestion -water leaching process is preferred in view of its excellent filtration properties. Subsequently, systematic digestion and leaching experiments showed that up to 97.1 % of Li was extracted under the optimized conditions, and the concentration of Li in the leach liquor is as high as 29.33 g/L. After pH adjustment and Al removal, Na 2 CO 3 precipitation were adopted for Li 2 CO 3 production. The equilibrium relationship in Li 2 SO 4 -Na 2 CO 3 -H 2 O system was analyzed to predict the precipitation behavior of Li and select appropriate operation window for Li 2 CO 3 preparation. Finally, with an additional carbonation -decomposition process, a Li 2 CO 3 product with a purity of 99.51 % is produced. This process realizes efficient synthesis of battery -grade Li 2 CO 3 from the intermediate product Li 2 SiO 3 .

Preparation of Li2CO3 Nanoparticles by Carbonation Reaction Using a Microfiltration Membrane Dispersion Microreactor

Preparation of Nano-CaCO3 from Phosphogypsum by Gas–Liquid–Solid Reaction for CO2 Sorption

Study on Catalytic Performance and Kinetics of High Efficiency CeO2 Catalyst Prepared by Freeze Drying for the Synthesis of Dimethyl Carbonate from CO2 and Methanol

Preparation of Li2CO3 by Gas‐liquid Reactive Crystallization of LiOH and CO2

Controllable Preparation of Sio2 Nanoparticles Using A Microfiltration Membrane Dispersion Microreactor

Process intensification for the synthesis and purification of battery-grade Li 2 CO 3 with microfluidics

Enhancement of Mixing and Mass Transfer Performance with a Microstructure Minireactor for Controllable Preparation of CaCO3 Nanoparticles

Preparation of battery-grade Li2CO3 efficiently by high shear dispersion at low temperature

Coupled reaction and solvent extraction process to form Li2CO3: Mechanism and product characterization

Mechanochemistry synthesis of high purity lithium carbonate

Preparation of Lithium Carbonate from a Li-bearing Desorption Solution

A Size-Controllable Precipitation Method to Prepare CeO2 Nanoparticles in a Membrane Dispersion Microreactor

A New Method for Direct Synthesis of Li2CO3 Powders by Membrane Electrolysis

An Efficient Approach for Preparation of Battery-Grade Li2CO3 from Intermediate Product Li2SiO3

Preparation of Ultrafine Calcium Carbonate with Micropore Dispersion

Preparation of nano-CeO2 and its application to synthesis of Dimethyl carbonate by liquid phase catalysis

Microbubble-assisted pressure carbonation for preparation of high purity lithium carbonate

Effects Of Various Factors On Biogas Purification And Nano-Caco3 Synthesis In A Membrane Reactor

Preparation method for lithium silicate CO2 adsorbent

Preparation of Nanofluids and Their Applications in Enhanced CO2 Absorption

Selective Synthesis of LiOH from High-Sodium Concentration Li2CO3 Mother Liquor