Study on the Thermal Degradation Kinetics of Biodegradable Poly(propylene carbonate) during Melt Processing by Population Balance Model and Rheology

shanshan lin,wei yu,xianhong wang,chixing zhou

DOI: https://doi.org/10.1021/ie404049v

2014-01-01

Industrial & Engineering Chemistry Research

Abstract:The degradation behavior of poly(propylene carbonate) (PPC) was investigated during melt processing to infer the mechanism and kinetics of thermal degradation. First, the degradation experiments were carried out in a miniature conical twin-screw extruder at different temperatures, rotating speeds, and processing times. Gel permeation chromatography (GPC) was applied to analyze the molecular weight and molecular weight distributions (MWDs) of melt processed PPC samples. The degradation process at various processing conditions was described by the population balance equations (PBEs) with random chain scission and chain end scission. By comparing the prediction of PBE model with the experimental evolution of molecular weight, it is proposed that random chain scission and chain end scission occur simultaneously. At temperature higher than 160 °C, random chain scission dominates with the activation energy about 120 kJ/mol. Second, a method combining the PBE model and rheology was suggested to determine the kinetics of degradation directly from the torque of mixer during melt processing without further measurements on molecular weight. Such method was applied to melt mixing of PPC in a batch mixer, from which a higher kinetic parameter of thermal degradation and similar activation energy were successfully determined as compared to those obtained from extrusion experiments.