Abstract:Good gas permeability is an essential factor for the smooth operation and high performance in the lower part of the blast furnace. Under the present low carbon blast furnace smelting conditions, the coke layer is thinner, and the proportion of the molten metal in the coke layer is significantly higher, resulting in a major reduction in gas permeability, which seriously affects blast furnace operations. Also, the lower thickness of the coke layer weakens the process of solid-liquid carbon dissolution when the molten iron passes through the coke layer, which reduces the carbon content of the molten iron and further deepens the erosion of the refractory by the unsaturated molten iron. The carbon dissolution in the molten iron in a blast furnace core was measured by a high-temperature vacuum wettability test tool that analyzed the interface wetting activity between Fe−C melts with specific carbon mass fraction (3.8%, 4.3%, 4.8%) and 99.9% of high temperatures graphite plates. Besides, the scanning electron microscope (SEM) and energy dispersive spectroscopy (EDS) were used to analyze the graphite substrate’s carburizing morphology and carburizing distances. The results show that, with the increase of carbon content, the interface contact angle becomes bigger. The contact angle decreases with time, and eventually reaches a steady-state during the melting process, and the Fe−C melt with saturated carbon cannot be wet. The scanning electron microscopy analysis shows that a spherical cap-like depression is created by a cross-section of the Fe−C melt and the graphite substrate, and the radius and volume of the depression decrease with increasing carbon content. The study of the EDS scanning analysis shows that the amount of dissolved carbon atoms in the graphite substrate penetrates the Fe−C melt and decreases with increasing initial carbon concentration. The smaller the carburizing effect, the better the wetting is conducive to carbon mass transfer. It is found that by measuring carburizing of the carbon atoms in the graphite substrate into the Fe−C melt by calculating the surface energy reduces the surface energy between the two. Thus, the surface tension decreases and the melt spreads slowly with contact angle gradually decreasing during melting.

Reduction of nickel-copper matte/oxysulfide/slag

Ignition and combustion of synthetic nickel mattes in simulated flash smelting conditions

Modeling of Exchange Interactions in Melts Formed During Joint Smelting of Oxidized Nickel Ores and Pyrrhotite Concentrates

Recovery of Fe, Ni, Co, and Cu from Nickel Converter Slag through Oxidation and Reduction

Optimization of converting process for matte of oxidized nickel ores and sulfide copper ores joint smelting based on thermodynamic simulation

Interface Wetting Behavior Between Iron and Coke During the Carbon Dissolution Process in a Blast Furnace

Numerical Investigation of the Limit of Coke Rate Reduction in an Ironmaking Blast Furnace (BF)

Control of Copper Content in Flash Smelting Slag and the Recovery of Valuable Metals from Slag—A Thermodynamic Consideration

Effect Of Roasting Temperature On Phase Transformation In Co-Reduction Roasting Of Nickel Slag

Reduction of Magnetite from Copper Smelting Slag in the Presence of a Graphite Rod

Artificial Slags with Modulated Properties for Controlled Nickel Dissolution in Smelting Process

Enhancing Rotary Kiln-Electric Furnace Process of Saprolitic Laterite from the Viewpoint of Slag Optimization to Minimize Energy Consumption

Recovery of Metals from Copper Smelting Slag Using Coke and Biochar

Characterization of fluidized reduction roasting of nickel laterite ore under CO/CO2 atmosphere

MATTE-SLAG SEPARATION BEHAVIOR AS A FUNCTION OF IRON PHASE REDUCTION IN COPPER SLAG

Reduction-Sulfurization Smelting Process of Waste Hydrogenation Catalysts, Automotive Exhaust Purifier Waste Catalysts, and Laterite Nickel Ore

Behavior of chromium in the reduction and smelting of high alumina nickel laterite in blast furnace

Catalytic reduction of nitrogen monoxide using iron–nickel oxygen carriers derived from electroplating sludge: Novel method for the collaborative emission decrease of polluting gases

Effect of B2O3 on the Melting Characteristics and Slag-Matte Separation of Nickel Flash Furnace Melting

Experimental Determination of the Main Parameters of the Refining Process of Rough Ferronickel, Obtained by Iron-Chromium-Nickel Selective Reduction

Experimental Study on the Phase Equilibrium of Copper Matte and Silica-Saturated FeO X -Sio 2 -Based Slags in Pyrometallurgical WEEE Processing