Investigation on comprehensive utilisation of nickel slag from JNMC
Jian Pan,Guolin Zheng,Deqing Zhu,Yu Cui
2010-01-01
Abstract:While manufacturing various kinds of nickel products to meet the increasing demand of our society, nickel plants have discarded plenty of slag containing nickel, iron or other valuable metals, which not only wastes resources, but pollutes the vulnerable environment, so it is pressing to take measures to make full use of this kind of slag by utilising those useful elements comprehensively. However, the recovery of nickel and copper in nickel slag from JNMC is difficult because of their low content in the slag and their diffusion into iron structure. When much of the iron is reduced, the percentage of non-ferrous metals in the product would be relatively low, decreasing their value. Therefore, it is of significant importance to control the reduction of iron in order to obtain high-degree nickel or copper product, which is desirable in the processing steps followed. It's also necessary to minimise the consumption of fuels and other types of energy by means of low-temperature reduction. In this paper, Slag JS, assaying 0.90 per cent Ni, 0.34 per cent Cu, 37.00 per cent Fe, and Slag JH, assaying 0.0095 per cent Ni, 0.98 per cent Cu, 38.07 per cent Fe, from JNMC were investigated through selective reduction-wet magnetic separation and direct reduction-wet magnetic separation respectively. The effect of basicity, reducing temperature, reducing time and the dosage of coal on the reduction of nickel slag was examined and the parameters in the process were optimised. It is showed that, for slag JS, concentrate containing 3.25 per cent Ni, 1.20 per cent Cu, 75.26 per cent Fe, was achieved with a yield of 20.00 per cent and recoveries of 82.20 per cent, 80.00 per cent, 42.17 per cent for Ni, Cu and Fe respectively at the following condition: basicity 0.15, reducing at 1200°C for 20 min, five per cent coal in blends, the magnetic intensity 131.34 KA/m; for slag JH, at optimal condition (basicity 0.18, reducing at 1050°C for 100 min, the mass ratio of coal to ore being 3:1, the magnetic intensity 75.62 KA/m), concentrate of 75.99 per cent Fe and 2.31 per cent Cu, was obtained with a yield of 33.15 per cent and recoveries of 66.06 per cent, 87.02 per cent for Fe and Cu respectively. © (2010) by the Australasian Institute for Mining and Metallurgy (AusIMM).