Abstract:The recovery of metal from copper slag is of great significance to the resource utilization of copper slag and the sustainable development of copper smelting industry. Currently, hydrometallurgy is the traditional method used to recover mineral metals. However, as copper slag is a silicate mineral, the traditional acid-leaching process of metal results in the leaching of Si, resulting in the formation of silica gel. The silica gel can inhibit the recovery of metal while making metal difficult to separate from Si and causing filtration problems. This study proposed a two-stage method (evaporation + water washing) to selectively recover Fe and Zn from copper slag. Under the optimal conditions (evaporation: H 2 SO 4 = 3 M; time = 60 min; temperature = 120°C; and liquid–solid ratio = 4; water washing: liquid–solid ratio = 5), the leaching efficiency of Fe, Zn, and Si reached 99.94 %, 97.40 %, and 0.15 % respectively. The separation mechanism was determined through mineral characterization (XRD, SEM, HRTEM-EDS, SAED, AFM, etc.) and the application of DLVO theory. It was found that H + destroyed the Fe 2 SiO 4 structure in copper slag during the evaporation stage, which promoted the release of Fe and Zn, forming soluble sulfate crystals. Simultaneously, evaporation increased the ion concentration, reducing the repulsive force between colloids, resulting in the aggregation and precipitation of silica gel into stable amorphous silica. After washing, soluble sulfate is dissolved in water. The recovered Fe can be processed to get red iron oxide (96.32 % purity), the Zn-containing solution can be recycled for electrolytic Zn, and the residue can be used to prepare geopolymer (52.47 MPa, 28 days). The two-stage method for recovering metals from copper slag is highly efficient and provides valuable insights into resource utilization of metals and Si in silicon-containing solid wastes.

Comprehensive Recovery of Multisource Metallurgical Wastes: Recycling Nickel Slag by Aluminum Dross with Converter-Slag Addition

Recovery of valuable metals from electroplating sludge with reducing additives via vitrification

Recovery of Valuable Metals from Nickel Smelting Slag Based on Reduction and Sulfurization Modification

Efficient Recycling of Valuable Metals from Waste Copper Slag by Using Secondary Aluminum Dross as a Novel Reductant

Treating waste with waste: Metals recovery from electroplating sludge using spent cathode carbon combustion dust and copper refining slag

Recovery of Fe, Ni, Co, and Cu from Nickel Converter Slag through Oxidation and Reduction

A Thermodynamic and Experimental Assessment of the Recovery of Copper, Iron, Zinc, and Lead from Copper Slag

Synergetic modification of industrial basic oxygen furnace slag and copper slag for efficient iron recovery

An approach of cobalt recovery from waste copper converter slags using pig iron as capturing agent and simultaneous recovery of copper and tin

Advances in Recovery of Valuable Metals and Waste Heat from Copper Slag

Recovery of Cu-Fe Alloy from Copper Smelting Slag

Recovery of Cu and Ni in Electroplating Sludge by a Low-Temperature Alkaline Smelting Technique

Co-modification of BOF Slag and Copper Slag to Recover Valuable Metals by Carbothermal Reduction

Characterization, Concentration, and Speciation of Metal Elements in Copper Slag: Implications for Secondary Metal Recovery

Recovery of valuable metals from copper slag

Stepwise Utilization Process to Recover Valuable Components from Copper Slag

A metallurgical approach for separation and recovery of Cu, Cr, and Ni from electroplating sludge

Two-stage method recovery of metals from copper slag: Realize the resource utilization of all components

Slag design and optimization for iron capturing platinum group metals from alumina-based spent catalysts

Effect Of Roasting Temperature On Phase Transformation In Co-Reduction Roasting Of Nickel Slag

Recovery of Valuable Metals and Production of Fe-V Crude Alloy from Vanadium-Enriched Slag Using Aluminum Dross as a Reductant