Abstract:An innovative technology for the direct reduction of copper slag was studied while smelting Cu-Fe alloy by carbon to recover the main valuable elements from the copper smelting slag. The melting temperature of samples first decreased, followed by an increase in Fe3O4 content in slag. The melting temperature reached the minimum temperature of 1157 °C once the Fe3O4 content was about 8 wt%. The recovery rate of copper and iron first increased gradually, followed by a rapid increase in the modifier (CaO). Subsequently, the rise in the recovery rate slowed down. The reduction rate of copper and iron only increased by 1.61% and 1.05% from 5 wt% CaO to 10 wt% CaO, but significantly increased by 8.89% and 14.21% from 10 wt% CaO to 25 wt% CaO, and remained almost unchanged beyond 25 wt% CaO. This could be attributed to the reaction between modifier (CaO) and silicate in acidic copper slag to generate low melting point composite oxide while replacing free iron oxides, improving the melting properties and reduction reaction. Meanwhile, the recovery rates of copper and iron increased with the increase of reaction time, reaction temperature, and reduction agent in a certain range. To obtain good element yield, the optimum conditions for reducing copper and iron from the molten copper slag were determined to be 1500 °C, 14 wt% C, 20–25 wt% CaO, and 60–80 min. The recovery rates of iron and copper reached about 90% and 85%, and the contents of iron and copper in alloy reached about 91–93 wt% and 5–7 wt%, respectively. The tailing was mainly composed of Ca3Si3O9, Ca(Mg,Al)(Si,Al)2O6, and SiO2, which could be used as a raw material for cement and pelletizing.

Reduction of Magnetite from Copper Smelting Slag in the Presence of a Graphite Rod

Investigation of Reducing Magnetite in Copper Slag Using CO–CO2

Research on kinetic of carbon reducing process of molten CaO-FeOx-SiO2 system

Experimental study on the copper slag reduction process

Evolution of the structure and viscosity of copper slag during metallization-reduction

Research on Selective Reducing Impoverishment Process of Copper Slag

Reduction of Copper Smelting Slag by Carbon for Smelting Cu-Fe Alloy

Reduction Kinetics of Copper Slag by H2

MATTE-SLAG SEPARATION BEHAVIOR AS A FUNCTION OF IRON PHASE REDUCTION IN COPPER SLAG

Reaction kinetics of smelting reduction for phosphorous production with magnesium phosphate slag

Mechanism of Composite Additive in Promoting Reduction of Copper Slag to Produce Direct Reduction Iron for Weathering Resistant Steel

Recovery of Iron from Copper Slag Using Coal-Based Direct Reduction: Reduction Characteristics and Kinetics

Investigation of Reducing Copper Slag Using Waste Motor Oil to Recover Matte

Direct reduction of copper slag using rubber seed oil as a reductant: Iron recycling and thermokinetics

Thermodynamic and kinetic behaviours of copper slag carbothermal reduction process

Investigation of Direct Reduction of Copper Slag Using Castor Oil as a Green Reductant: Metal Recovery, Reduction Characterization and Kinetic Analysis

Reductive Roasting Mechanism of Copper Slag and Nickel Laterite for Fe-Ni-Cu Alloy Production

Effect of Iron Phase Evolution on Copper Separation from Slag Via Coal-Based Reduction

REDUCTIVE-SULFURIZING SMELTING TREATMENT OF SMELTER SLAG FOR COPPER AND COBALT RECOVERY

Direct reduction of copper slag-carbon composite pellets by coal and biochar

A Novel Process to Upgrade the Copper Slag by Direct Reduction-Magnetic Separation with the Addition of Na2CO3 and CaO