Abstract:Over 50 million tons of copper slag are produced worldwide annually. Stacking is currently the primary method used to treat copper slag, resulting in resource wastage and environmental issues. Using slag as a raw material in the steel industry is areasonablesolution. However, the presence of nonferrous metals degrades steel performance and corrodes smelting equipment, and the remaining slag poses environmental and sustainable challenges. Thus, this study focused on removal of nonferrous metals from copper slag and subsequent reduction of iron oxide. The experimental results showed that increasing the percentage of the chlorinating agent (calcium chloride), temperature, and duration, the removal percentage of copper initially increased linearly, then plateaued. The acidity coefficient had a marginal effect on copper removal percentage. The optimum chlorination roasting conditions were 13 % calcium chloride, 1373 K, and 0.5 h, resulting in removal percentages of 90.3 %, 81.9 %, and 82.7 % for copper, zinc, and lead, respectively. The appropriate oxygen partial pressure for chlorination roasting was 10-5-0.7 atm. The reduction percentage of iron oxide was approximately 82 % under roasting conditions of 1.5 h at 1373 K. Based on these results, a novel scheme for copper slag utilization is proposed that involves chlorination roasting for nonferrous metal removal, reduction roasting for iron oxide reduction, and melting to obtain molten iron and separate molten slag. The iron and slag are used for steel manufacturing and rock wool preparation, respectively. This scheme provides apromisingway to efficiently use copper slag, which will reduce primary resource consumption and pollution.

Investigation of Reducing Copper Slag Using Waste Motor Oil to Recover Matte

Copper Smelting Slag Cleaning in an Electric Furnace by Using Waste Cooking Oil

Investigation of Direct Reduction of Copper Slag Using Castor Oil as a Green Reductant: Metal Recovery, Reduction Characterization and Kinetic Analysis

Distribution of copper and iron components with hydrogen reduction of copper slag

Cracking of waste cooking oil in the presence of copper slag

An efficient approach to utilize copper smelting slag: Separating nonferrous metals and reducing iron oxide at high temperature

Direct reduction of copper slag using rubber seed oil as a reductant: Iron recycling and thermokinetics

Investigation of Reducing Magnetite in Copper Slag Using CO–CO2

Energy conservation and emission reduction through utilization of latent heat of copper slag for iron and copper recovery

Insight into the function of waste cooking oil in the magnetite reduction process

A Thermodynamic and Experimental Assessment of the Recovery of Copper, Iron, Zinc, and Lead from Copper Slag

Efficient Recycling of Valuable Metals from Waste Copper Slag by Using Secondary Aluminum Dross as a Novel Reductant

A green method to clean copper slag and rapidly recover copper resources via reduction-sulfurizing smelting and super-gravity separation at low temperature

Efficiency improvements of the CO-H2 mixed gas utilization related to the molten copper slag reducing modification

Stepwise Utilization Process to Recover Valuable Components from Copper Slag

Reduction of Magnetite from Copper Smelting Slag in the Presence of a Graphite Rod

Reduction of Copper Smelting Slag by Carbon for Smelting Cu-Fe Alloy

Manufacture of wear-resistant cast iron and copper-bearing antibacterial stainless steel from molten copper slag via vortex smelting reduction

Eco-friendly iron extraction from fe-containing copper smelting slag via reduction roasting with coal and magnetic separation: Experimental and mechanism insights

Thermodynamic Phase Conversion Mechanism on Copper–Cobalt Slag Cleaning Process Using Gypsum Wastes as Sulfurizing Agent

Recovery of iron from waste slag of pyrite processing using reduction roasting magnetic separation method