Abstract:An innovative technology for the direct reduction of copper slag was studied while smelting Cu-Fe alloy by carbon to recover the main valuable elements from the copper smelting slag. The melting temperature of samples first decreased, followed by an increase in Fe3O4 content in slag. The melting temperature reached the minimum temperature of 1157 °C once the Fe3O4 content was about 8 wt%. The recovery rate of copper and iron first increased gradually, followed by a rapid increase in the modifier (CaO). Subsequently, the rise in the recovery rate slowed down. The reduction rate of copper and iron only increased by 1.61% and 1.05% from 5 wt% CaO to 10 wt% CaO, but significantly increased by 8.89% and 14.21% from 10 wt% CaO to 25 wt% CaO, and remained almost unchanged beyond 25 wt% CaO. This could be attributed to the reaction between modifier (CaO) and silicate in acidic copper slag to generate low melting point composite oxide while replacing free iron oxides, improving the melting properties and reduction reaction. Meanwhile, the recovery rates of copper and iron increased with the increase of reaction time, reaction temperature, and reduction agent in a certain range. To obtain good element yield, the optimum conditions for reducing copper and iron from the molten copper slag were determined to be 1500 °C, 14 wt% C, 20–25 wt% CaO, and 60–80 min. The recovery rates of iron and copper reached about 90% and 85%, and the contents of iron and copper in alloy reached about 91–93 wt% and 5–7 wt%, respectively. The tailing was mainly composed of Ca3Si3O9, Ca(Mg,Al)(Si,Al)2O6, and SiO2, which could be used as a raw material for cement and pelletizing.

Experiment on Reducing Agent for Recovering Iron from Pyrite Sulfur Refining Slag by Reduction Roasting and Magnetic Separation

Recovery of iron from waste slag of pyrite processing using reduction roasting magnetic separation method

Study on Separation of Iron from Waste Slag of Pyrite Processing

Recovery of iron from pyrite cinder by suspension magnetization roasting-magnetic separation method: Process optimization and mechanism study

Experimental study on the copper slag reduction process

Recovery of valuable elements from pyrite pyrolysis slag using magnetic separation-flotation technique

Study on Iron Extraction from High Iron Bauxite Residue by Pyrite Reduction

Effect of Temperature on Recovery of Iron from Waste Slag of Pyrite Processing

Experiments on the Coal-based Direct Reduction-Magnetic Separation of a Refractory Iron Ore

Probing Study on Separating Pb, Zn, and Fe from Lead Slag by Coal-based Direct Reduction

Effects of Fluxing Agent on Direct Reduction of Some Low-grade Iron Ore

Recovery of Iron from Copper Slag Using Coal-Based Direct Reduction: Reduction Characteristics and Kinetics

Preparation of Direct Reduction Sponge Iron (DRI) Using Pyrite Cinder Containing Nonferrous Metals

Recovery of Copper, Lead and Zinc from Copper Flash Converting Slag by the Sulfurization-Reduction Process

Improved iron recovery from low-grade iron ore by efficient suspension magnetization roasting and magnetic separation

Reduction of Copper Smelting Slag by Carbon for Smelting Cu-Fe Alloy

Effects of Reductants on the Reduction Roasting and Fe-P Separation of High Phosphorus Oolitic Hematite

Properties of flash roasted products from low-grade refractory iron tailings and improvement method for their magnetic separation index

Reduction of Magnetite from Copper Smelting Slag in the Presence of a Graphite Rod

Study on the factors affecting the deep reduction of coal gangue containing high contents of iron and sulfur

Direct reduction of copper slag using rubber seed oil as a reductant: Iron recycling and thermokinetics