Abstract:The PSf casting solution required degassing, sealing, and humidity and temperature control.PA layer formation on the top surface of the PSf substrate resulted in the highest FO performance.GO modification of the PA layer considerably enhanced water flux and reduced reverse solute fluxThe FO membranes exhibited high rejection efficiency for dyes used in the textile industry.The application of FO for water recovery is economic and environmentally friendly.In this study, the preparation procedures for the polysulfone (PSf) substrate and polyamide (PA) selective layers were systematically investigated to determine their effects on the separation performance of thin-film composite (TFC) forward osmosis (FO) membranes in terms of the permeate flux (Jw) and reverse solute flux (Js). Furthermore, the PA active layer was modified by adding different proportions of an emerging material, graphene oxide (GO), to increase Jw and decrease Js. The experimental results indicated that special attention should be paid to the preparation of the PSf casting solution, which required thorough degassing, sealing, and humidity and temperature control. The optimum casting height was discovered to be 175 μm. For PA layer formation, the same amount of polymer solutions (resulting thickness of 78.5 μm) on the top surface of the PSf substrate (on the side facing the water during phase inversion) resulted in the highest FO performance. GO modification of the PA layer at the dosage of 0.0175 wt% considerably enhanced Jw to 14 L m−2 h−1 and reduced Js to 0.23 mol m−2 h−1. However, higher GO dosage (0.02 wt%) led to lower membrane performance due to aggregation of GO nanoparticles, as confirmed using scanning electron microscopy. Next, the prepared membranes were applied to dye rejection and sludge concentration for water recovery. The virgin and modified FO membranes both exhibited high rejection efficiency (≥ 96.0%) for dyes commonly used in the textile industry. The 0.0175%-GO-modified FO membrane exhibited a higher concentration factor (1.67) and greater water recovery (40.0%) than the virgin membrane (1.45 and 31.2%, respectively). Therefore, the application of FO for water recovery is economic and environmentally friendly in terms of saving the transportation cost of sludge disposal while recovering water for reuse in wastewater treatment plants.

Graphene oxide incorporated thin-film composite membranes for forward osmosis applications

Graphene Oxide Based Membrane Intercalated by Nanoparticles for High Performance Nanofiltration Application

Role of Graphene Oxide in Support Layer Modification of Thin Film Composite (TFC) Membrane for Forward Osmosis Application

Graphene Oxide-Based Membranes Intercalated with an Aromatic Crosslinker for Low-Pressure Nanofiltration

Electrospun nanofiber based forward osmosis membrane using graphene oxide as substrate modifier for enhanced water flux and rejection performance

Porous graphene oxide surface-coated thin-film composite membrane for simultaneously increasing permeation performance and organic-fouling migration capacities

Graphene Oxide Modified Graphitic Carbon Nitride As A Modifier for Thin Film Composite Forward Osmosis Membrane

Fabrication and modification of forward osmosis membranes by using graphene oxide for dye rejection and sludge concentration

Fabrication of high performance TFN membrane incorporated with graphene oxide via support-free interfacial polymerization

Functionalised graphene oxide-based nanofiltration membranes with enhanced molecular separation performance

Enhancing H2O2 Tolerance and Separation Performance through the Modification of the Polyamide Layer of a Thin-Film Composite Nanofiltration Membrane by Using Graphene Oxide

Construction of facilitated mass transfer composite membrane with triple-layer water nanochannel architecture for forward osmosis process using cGO-coated polysulfone separation membrane as the substrate

Development of high-performance electrospun nanofiber based forward osmosis membrane by introducing graphene oxide‐calcium carbonate particle composite intermediate layer

A novel polyamide thin-film nanocomposite reverse osmosis membrane constructed by a 3D multi-layer graphene oxide assembled with 1,3-diamino-2-propanol

Fabrication of organic solvent nanofiltration membranes with graphene oxide - Enhanced covalent organic framework via interfacial polymerization

Graphene Oxide Membranes for Ionic/Molecular Filtration: from Self-Assembly to Design

Chemically Cross-Linked Graphene Oxide as a Selective Layer on Electrospun Polyvinyl Alcohol Nanofiber Membrane for Nanofiltration Application

Fabrication and characterization of high-performance forward-osmosis membrane by introducing manganese oxide incited graphene quantum dots

Effect of poly(2-(dimethylamino)ethyl methacrylate) brush-grafted graphene oxide on polyamide layer formation and nanofiltration performance

Enhanced permeability and biofouling mitigation of forward osmosis membranes via grafting graphene quantum dots

Incorporating functionalized graphene oxide into diethylene triamine-based nanofiltration membranes can improve the removal of emerging organic micropollutants