Abstract:The PSf casting solution required degassing, sealing, and humidity and temperature control.PA layer formation on the top surface of the PSf substrate resulted in the highest FO performance.GO modification of the PA layer considerably enhanced water flux and reduced reverse solute fluxThe FO membranes exhibited high rejection efficiency for dyes used in the textile industry.The application of FO for water recovery is economic and environmentally friendly.In this study, the preparation procedures for the polysulfone (PSf) substrate and polyamide (PA) selective layers were systematically investigated to determine their effects on the separation performance of thin-film composite (TFC) forward osmosis (FO) membranes in terms of the permeate flux (Jw) and reverse solute flux (Js). Furthermore, the PA active layer was modified by adding different proportions of an emerging material, graphene oxide (GO), to increase Jw and decrease Js. The experimental results indicated that special attention should be paid to the preparation of the PSf casting solution, which required thorough degassing, sealing, and humidity and temperature control. The optimum casting height was discovered to be 175 μm. For PA layer formation, the same amount of polymer solutions (resulting thickness of 78.5 μm) on the top surface of the PSf substrate (on the side facing the water during phase inversion) resulted in the highest FO performance. GO modification of the PA layer at the dosage of 0.0175 wt% considerably enhanced Jw to 14 L m−2 h−1 and reduced Js to 0.23 mol m−2 h−1. However, higher GO dosage (0.02 wt%) led to lower membrane performance due to aggregation of GO nanoparticles, as confirmed using scanning electron microscopy. Next, the prepared membranes were applied to dye rejection and sludge concentration for water recovery. The virgin and modified FO membranes both exhibited high rejection efficiency (≥ 96.0%) for dyes commonly used in the textile industry. The 0.0175%-GO-modified FO membrane exhibited a higher concentration factor (1.67) and greater water recovery (40.0%) than the virgin membrane (1.45 and 31.2%, respectively). Therefore, the application of FO for water recovery is economic and environmentally friendly in terms of saving the transportation cost of sludge disposal while recovering water for reuse in wastewater treatment plants.

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to develop an efficient forward osmosis (FO) membrane to address the problems such as high energy consumption and easy pollution in traditional pressure - driven membrane separation technologies. Specifically, the author modifies the polyamide (PA) active layer by using graphene oxide (GO) in order to increase the water flux (\(J_w\)) of the FO membrane while reducing the reverse solute flux (\(J_s\)). In addition, the study also explores the effects of factors such as the preparation conditions of the PSf substrate solution (such as environmental humidity and temperature), the casting height of the PSf substrate, and the proportion of the PA polymerization solution on the performance of the FO membrane, thereby determining the most suitable preparation conditions. To verify the practical application effect of the prepared FO membrane, the researchers applied it to dye retention and water recovery from concentrated sludge to evaluate its potential in textile industry wastewater treatment and sludge dehydration in sewage treatment plants. The experimental results show that the FO membrane modified with 0.0175 wt% GO exhibits a higher water recovery rate (40.0%) and concentration factor (1.67), compared with the unmodified membrane (31.2% and 1.45 respectively), showing good application prospects. In summary, this research mainly solves the following problems: - Increase the water flux of the FO membrane and reduce the reverse solute flux. - Systematically evaluate the key preparation parameters that affect the performance of the FO membrane. - Verify the application effect of the modified FO membrane in actual wastewater treatment.

Fabrication and modification of forward osmosis membranes by using graphene oxide for dye rejection and sludge concentration

Graphene Oxide Based Membrane Intercalated by Nanoparticles for High Performance Nanofiltration Application

Electrospun nanofiber based forward osmosis membrane using graphene oxide as substrate modifier for enhanced water flux and rejection performance

Construction of facilitated mass transfer composite membrane with triple-layer water nanochannel architecture for forward osmosis process using cGO-coated polysulfone separation membrane as the substrate

Fabrication of high performance TFN membrane incorporated with graphene oxide via support-free interfacial polymerization

Antifouling forward osmosis membranes by ε-polylysine mediated molecular grafting for printing and dyeing wastewater: Preparation, characterization, and performance

Role of Graphene Oxide in Support Layer Modification of Thin Film Composite (TFC) Membrane for Forward Osmosis Application

Development of high-performance electrospun nanofiber based forward osmosis membrane by introducing graphene oxide‐calcium carbonate particle composite intermediate layer

Enhancing water recovery through integrated graphene oxide-modified forward osmosis and membrane distillation for real textile wastewater treatment

Fabrication and characterization of high-performance forward-osmosis membrane by introducing manganese oxide incited graphene quantum dots

Enhancing H2O2 Tolerance and Separation Performance through the Modification of the Polyamide Layer of a Thin-Film Composite Nanofiltration Membrane by Using Graphene Oxide

Effect of poly(2-(dimethylamino)ethyl methacrylate) brush-grafted graphene oxide on polyamide layer formation and nanofiltration performance

Polydopamine nanoparticles modified nanofiber supported thin film composite membrane with enhanced adhesion strength for forward osmosis

Sulfonated graphene oxide modified polysulfone-polyamide forward osmosis membrane and its application in fluorine-containing wastewater treatment

Graphene Oxide Modified Graphitic Carbon Nitride As A Modifier for Thin Film Composite Forward Osmosis Membrane

Highly Permeable PA@GO Loose Nanofiltration Membranes Enabled by Hierarchical Transport Channels for Efficient Dye Removal

Surface engineering of graphene oxide membranes for selective separation of perfluorooctanoic acids

Towards enhanced performance of fertilizer-drawn forward osmosis process coupled with sludge thickening using a thin-film nanocomposite membrane interlayered with Mxene scaffolded alginate hydrogel

High performance Fabric-Reinforced sulfonated polysulfone supported thin film composite membrane

GO and surfactant assisted regulation of polyamide nanofiltration membranes for improved separation performance

Synthesis and characterization of porous reduced graphene oxide based geopolymeric membrane with titanium dioxide coating for forward osmosis application