Abstract:Equimolar AlCoCrFeNi high entropy alloy (HEA) with a coherent dual-phase structure commonly exhibits good strength at high temperatures. Regretfully, the poor oxidation resistance greatly limits its practical application space. In this work, the effect of the reactive element (RE) Y on the oxidation resistance of AlCoCrFeNi HEA is explored. (AlCoCrFeNi) 100- x Y x ( x = 0, 0.1, 0.5 and 1, at.%) were designed and their oxidation mechanisms were unravelled at 1100 °C. Besides the two original B2 phase and A2 phase, the Y-doped HEAs contain (Y, Ni)-rich phase. An appropriate amount of Y blocks the outward Al diffusion and meanwhile inhibits the laterally grown oxides within the existing scale, thereby suppressing the formation of interface pores and rumplings and contributing to superior resistance to oxide scale spallation. However, excessive Y doping causes the formation of (Y, Al)-rich oxide intrusions, which result in the nucleation of cracks near them and thus degrade the interface adherence. The generation and failure mechanisms of oxide scales formed on Y-doped HEAs during 100 h oxidation have been revealed. The presented information proposes new insights to improve the high-temperature oxidation resistance of AlCoCrFeNi HEA and may be useful for assessing the possibility of the practical application of HEAs in aerospace engine components.

The role of Dy and Hf doping on oxidation behavior of two-phase (γ′+β) Ni–Al alloys

A comparative study on the oxidation behavior of Y-, Hf- and YHf-doped NiCoCrAl alloys: effect of reactive elements

Effect of Y-doping on the microstructural evolution and oxidation resistance of NiAlHf coatings at 1200 °C

The influence of Hf content on oxide scale microstructure and HfO2 formation mechanisms in two-phase (γ' + β) Ni-Al alloys

Effect of Substrate Characteristics on Interdiffusion Coefficients of Ni and Al Atoms in Β-Nial Phase of Aluminide Coatings

Oxidation Mechanism of Three Fe-Al Alloys with and Without Addition of 0.1 At% Yttrium at 800 °C

Effect of Al content on the oxidation behavior of NiCoCrAlYHf alloys at 1100°C

Effect of Hf as oxygen vacancy formation inhibitor on the oxidation behavior of Ni-28 W alloy

Effect of Al content on the oxidation behavior of Y/Hf-doped AlCoCrFeNi high-entropy alloy

The effect of Re and Hf interaction on the oxidation performance in ReHf co-doped NiAl coating

Surface Rumpling Behavior of Hf/Zr Single-Doped and Co-Doped β-NiAl Coatings during High-Temperature Cyclic Oxidation

Unraveling the oxidation mechanism of Y-doped AlCoCrFeNi high-entropy alloy at 1100 °C

Investigation of Pt-Dy Co-Doping Effects on Isothermal Oxidation Behavior of (Co,ni)-Based Alloy

Mechanical Properties and Oxidation Characteristics of TiNiAl(Nb) Intermetallics

Oxidation behavior of high Hf nickel-based superalloy in air at 900, 1000 and 1100°C

Y/Hf-doped Al0.7CoCrFeNi high-entropy alloy with ultra oxidation and spallation resistance at 1200 °C

Investigation on the microstructural evolution and oxidation resistance of Ru-doped NiAlHf coatings at 1200 °C

Microstructure and oxidation behavior of the Y/Ta/Hf co-doped AlCoCrFeNi high-entropy alloys in air at 1100 °C

Microstructural evolution and element interdiffusion of NiAlHf and NiAlHfY coatings deposited on a Ni-based superalloy

The importance of grain boundaries on the reactive elements effect in β-NiAlHf alloy

Effect of Pt Doping on Oxide Scale Formation on Yttria-Dispersion FeCrAl Alloy at 1200℃