Abstract:Hot pressing was used to produce compact ceramic samples with the following composition (wt.%): 60 ZrB2 + 20 SiC + 20 (Al2O3 + 32 t-ZrO2). The tetragonal modification of zirconium oxide in the eutectic was stabilized by yttrium oxide. The porosity of the samples was 3–5%. The mechanical properties of the ceramics (hardness HV, fracture toughness KIc, tensile strength δf, compressive strength Y, grain-boundary strength S, and bending strength σ) were studied. Analysis of the microstructure and elemental composition of the phases revealed that a defect-free structure developed in the ZrB2-based composite through strong Van Der Waals adhesive interaction at the SiC–Al2O3 interface, which increased the fracture toughness to 9.4 MPa ∙ m1/2. In turn, this increased the grain strength from 0.64 GPa for the basic composite to 3.46 GPa for the ZrB2–SiC composite with an oxide addition. An addition of Al2O3 + 32 wt.% t-ZrO2 was introduced in sufficient quantities not only to reduce the fracture stress but also to promote plastic deformation of the material for high-temperature bending strength. Study of the oxidation process showed that the weight increment of the 60 wt.% ZrB2 + 20 wt.% SiC + 20 wt.% (Al2O3 + 32 wt.% t-ZrO2) sample at 1600°C for a holding time of 1 h was stabilized by dense oxide scale formed on the material, while the weight increment of the ZrB2 + 20 wt.% SiC sample and, consequently, the scale thickness increased monotonically. The scale that formed on the ZrB2 + 20 wt.% SiC samples with an addition of Al2O3 + 32 wt.% t-ZrO2 consisted of an upper Al2SiO5-based layer 50 μm thick with ZrO2 inclusions and a lower ZrO2-based layer up to 80 μm thick with Al2SiO5 inclusions. The eutectic Al2O3 + 32 wt.% t-ZrO2 oxide addition to the basic ZrB2–SiC system had higher oxidation resistance and thus prevented the diffusion of oxygen into the material.

Effect of Surface Oxidation on Thermal Shock Resistance of ZrB 2 –sic–zrc Ceramic at Temperature Difference from 800 to 1900 °C

Thermal Shock Behavior of Zrb2-Sic Ceramics with Different Quenching Media

Thermal shock behavior of SiC-whisker-reinforced diboride ultrahigh-temperature ceramics

Effect of boronizing treatment on the oxidation resistance of Zr2(AlSi)4C5/SiC composite

Enhanced Oxidation Resistance of ZrB2‐SiC‐WC Composite Below 1800 °C

The Oxidation of ZrB2/MoSi2 Ceramics in Dissociated Air: The Influence of the Elaboration Technique

Isothermal Oxidation of Zr2[Al(Si)]4C5–SiC Composites at 1000–1300°C in Air

Effect of repeated thermal shock on mechanical properties of ZrB2-SiC-BN ceramic composites

Thermal and Electrical Transport in ZrB2-SiC-WC Ceramics Up to 1800 °C

Oxidation behavior and kinetics of (Zr, Ti)(C, N)–SiC ceramics with enhanced oxidation resistance at 850 °C–950 °C

Effect of SiC Content on the Ablation and Oxidation Behavior of ZrB2-Based Ultra High Temperature Ceramic Composites

The Effect of MoAlB Substitutions on the Oxidation Behavior of ZrB2-SiC Composites at 1600°C

Effect of temperature-dependent nano SiC on the ablation resistance of ZrC coating

Study on Thermal Shock Resistance and Oxidation Resistance of Ultra-High Temperature Ceramics

Effects of Si3N4 and WC on the oxidation resistance of ZrB2/SiC ceramic tool materials

Preparation and flame ablation/oxidation behavior of ZrB2/SiC ultra-high temperature ceramic composites

Phase stability, hardness and oxidation behaviour of spark plasma sintered ZrB2-SiC-Si3N4 composites

High-Temperature Oxidation Resistance of ZrB2-SiC Ceramic Composites Prepared by Reactive Hot Pressing

The Oxidation Behavior of ZrB2-SiC Ceramic Composites Fabricated by Plasma Spray Process

Ablative properties of laminated ZrB2-SiC ceramic modified by SiC whisker in oxyacetylene environment

Mechanical and Corrosion Properties of ZrB2–SiC Composite Ceramics with Oxide Additions