Abstract:The development of high-speed aerial vehicles urgently requires high-performance integrated materials for ablation resistance, thermal insulation and oxidant protection under high temperature. The previously prepared carbon aerogel composites (C/CA), with ultra-high temperature thermal insulation properties, were impregnated with SiCO precursor sol and pyrolysed in nitrogen atmosphere at 1200?C. The impregnation/pyrolysis process was performed once, twice and thrice to obtain three different C/C-SiCO nanoporous ceramic composites. Further, TaSi2-MoSi2-borosilicate glass (TM-BG) coating or TaSi2-MoSi2-ZrB2-borosilicate glass (TMZBG) coating was prepared on the surface of the C/C-SiCO through slurry brushing combined with graphite powder embedded sintering process. By simulating the actual application environment through oxygen acetylene flame ablation test, the ablation resistance of the samples was studied and their oxidation mechanism was analysed. The results show that the ablation rate of the C/C-SiCO after 200 s ablation at 1600 ?C decreases with the increase of the number of impregnation/pyrolysis steps and that the ablation resistance of the coating modified C/C-SiCO was significantly enhanced. The addition of ZrB2 to the coating improves the compatibility between the substrates and the coating, and the TMZ-BG coated sample has better ablation resistance. At high temperature, the borosilicate glass in the coating is in a viscous flow state. Meanwhile the SiO2 generated by the oxidation of other silicide raw materials forms a dense glass layer on the coating surface, which can be used as an oxygen barrier to provide better protection for the substrates. The coating-modified C/C-SiCO porous ceramic composites are expected to be used as a high-temperature ablation-resistant material for the thermal protection system of new aerospace vehicles.

Ablative properties of laminated ZrB2-SiC ceramic modified by SiC whisker in oxyacetylene environment

Mechanical and plasma ablation properties of double-interface fibrous ZrB 2 -SiC ceramics for ultra-high-temperature application

Mechanical and ablation properties of laminated ZrB2-SiC ceramics with Si3N4 whisker interface

Preparation and flame ablation/oxidation behavior of ZrB2/SiC ultra-high temperature ceramic composites

Ablation behavior and mechanisms of 3D C<sub>f</sub>/ZrB<sub>2</sub>-SiC composite applied in long-term temperature up to 2400 C

Oxidation behavior and ablation mechanism of Cf/ZrB2-SiC composite fabricated by vibration-assisted slurry impregnation combined with low-temperature hot pressing

Ablation behavior and mechanisms of 3D Cf/ZrB2-SiC composite applied in long-term temperature up to 2400 °C

Structural characteristics and ablative behavior of C/C–ZrC–SiC composites reinforced with “Z-pins like” Zr–Si–B–C multiphase ceramic rods

Ultra-high-temperature ablation behavior of SiC–ZrC–TiC modified carbon/carbon composites fabricated via reactive melt infiltration

Ablation resistance behavior of ZrB2-SiC ultra-high temperature ceramics with Y2O3 addition

Ablation properties and mechanisms of BN-coated Cf-reinforced SiBCNZr ceramic composites under an oxyacetylene combustion torch

Effect of temperature-dependent nano SiC on the ablation resistance of ZrC coating

Ablation Behavior of ZrB2–SiC–ZrO2 Ceramic Composites by Means of the Oxyacetylene Torch

Ablation behavior and mechanisms of ZrC-SiC-MoSi2 coated C/C-SiC-ZrC ceramic matrix composites under oxyacetylene torch

Fabrication and Ablation Properties of SiC Nanowires-Network Modified Carbon/Carbon–Ultrahigh Temperature Ceramics Composites

Effect of surface microstructure on the temperature response of ZrB 2 –SiC composites

Long-term ablation behavior and mechanisms of 2D-Cf/ZrB2-SiC composites at temperatures up to 2400 °C

Effect of SiC Content on the Ablation and Oxidation Behavior of ZrB2-Based Ultra High Temperature Ceramic Composites

Multi-cycle and long-term ablation behavior of Cf/ZrB2-SiC composites at 2500 °C

Ablation resistance of C/C-SiCo nanoporous ceramic composites with TaSi2-MoSi2-ZrB2-borosilicate glass coating

Long-term Ablation Behavior of Al4SiC4-YB4 SiC4-YB4 Modified Cf/ZrB2-SiC F /Zrb2-Sic Composites at 2600 °C