Abstract:Resorbable Mg and Mg alloys have gained significant interest as promising biomedical materials. However, corrosion of these alloys can lead to premature reduction in their mechanical properties, and therefore their corrosion rate needs to be controlled. The aim of this study is to select an appropriate environment where the effects of coatings on the corrosion rate of the underlying Mg alloy can be discerned and measured in a relatively short time period. The corrosion resistance of uncoated AZ31 alloy in different solutions [Hank's Balanced Salt Solution, 1× phosphate buffered solution (PBS), 4× PBS, 0.9%, 3.5%, and 5 M sodium chloride (NaCl)] was determined by measuring the weight loss over a 2 week period. Upon exposure to physiological solutions, the uncoated AZ31 alloys exhibited a variable weight increase of 0.4 ± 0.4%. 3.5% and 5 M NaCl solutions led to 0.27 and 9.7 mm/year corrosion rates, respectively, where the compositions of corrosion products from AZ31 in all saline solutions were similar. However, the corrosion of the AZ31 alloy when coated by electrochemical oxidation with two phosphate coatings, one containing fluorine (PF) and another containing both fluorine and silica (PFS), showed 0.3 and 0.25 mm/year corrosion rates, respectively. This is more than 30 times lower than that of the uncoated alloy (7.8 mm/year), making them promising candidates for corrosion protection in severe corrosive environments. Cross-sections of the samples showed that the coatings protected the alloy from corrosion by preventing access of saline to the alloy surface, and this was further reinforced by corrosion products from both the alloy and the coatings forming an additional barrier. The information in this paper provides a methodology for evaluating the effects of coatings on the rate of corrosion of magnesium alloys.

Corrosion of Magnesium Alloy Az31: the Influence of Bicarbonate, Sulphate, Hydrogen Phosphate and Dihydrogen Phosphate Ions in Saline Solution

Exploring the Corrosion Performance of AZ31 Magnesium Alloy under Acidic and Alkaline Conditions

Influence of Aggressive Ions on the Degradation Behavior of Biomedical Magnesium Alloy in Physiological Environment

Roles of pH in the NH4+-induced corrosion of AZ31 magnesium alloy in chloride environment

Influence of Artificial Biological Fluid Composition on the Biocorrosion of Potential Orthopedic Mg-Ca, Az31, Az91 Alloys

Effect of CaCl2 and NaHCO3 in Physiological Saline Solution on the Corrosion Behavior of an As-Extruded Mg–Zn–Y–Nd alloy

Effect of Chemical Treatment on the Corrosion Behavior of Mg-2Zn-1Mn (ZM21) Magnesium Alloy

The Corrosion Behavior of AZ91D Magnesium Alloy in Simulated Haze Aqueous Solution

Effect of pH on the Corrosion Mechanism of Zinc Magnesium Aluminium Alloy Coatings for Steels

Evaluation of Corrosion Performance of AZ31 Mg Alloy in Physiological and Highly Corrosive Solutions

Corrosion Properties of AZ31 Magnesium Alloy and Protective Effects of Chemical Conversion Layers and Anodized Coatings

Effects of Inorganic Metabolites of Sulphate-Reducing Bacteria on the Corrosion of AZ31B and AZ63B Magnesium Alloy in 3.5 wt.% NaCl Solution

Inhibitive effect of sodium carbonate on corrosion of AZ31 magnesium alloy in NaCl solution

The Effect of Vanadate, Phosphate, Fluoride Compounds on the Aqueous Corrosion of Magnesium Alloy AZ31 in Dilute Chloride Solutions

Biodegradation of Az31 and We43 Magnesium Alloys in Simulated Body Fluid

Corrosion behavior of anodized AZ91D magnesium alloy in NaCl aqueous solution

Influence of ammonium sulfate on the corrosion behavior of AZ31 magnesium alloy in chloride environment

A Combined Inhibiting Effect of Sodium Alginate and Sodium Phosphate on the Corrosion of Magnesium Alloy Az31 in Nacl Solution

Lithium Carbonate and Oxalate Salts as Corrosion Inhibitors for Magnesium Alloy AZ31 B in NaCl Solution

Effects of Electric Parameters on Corrosion Resistance of Anodic Coatings Formed on Magnesium Alloys

Corrosion Behaviour of Az21, Az501 and Az91 in Sodium Chloride