Abstract:The anodic polarization response of magnesium alloy AZ31 was first characterized during exposure to aerated 0.1 M NaCl solutions with millimolar additions of NaVO3, Na3PO4, Na2HPO4, NaF and various pairings to assess their ability to inhibit corrosion kinetics and retard localized corrosion. Each of the candidate inhibitors reduced the corrosion rate of the alloy to some degree. A Na3PO4–NaVO3 pair produced a good inhibiting effect decreasing the corrosion rate to about 10−7 A/cm2, which was two orders of magnitude lower than the uninhibited control case. A Bliss Independence assessment indicated that this inhibitor pair acted synergistically. A Na2HPO4–NaVO3 pair reduced the corrosion rate to 10−6 A/cm2 but was not assessed to be acting synergistically. The NaVO3–NaF pair did not reduce the corrosion rate significantly compared to the control case and was an antagonistic pairing. SEM imaging showed film formation due to exposure, which appears to be the origin of the observed inhibition. The resistance to localized corrosion was assessed as the difference in the breakdown potential and the corrosion potential, with larger values indicating a lower probability of localized corrosion during free corrosion exposures. The effects of the inhibitors on this characteristic were mixed, but each of the inhibitor pairs yielded potential differences in excess of 100 mV. A conceptual conversion coating process based on a mixture of vanadate and phosphate compounds were demonstrated. A fluoride-bearing formulation produced coatings whose total impedance was increased by a factor of two compared to an uncoated control. A fluoride-free formulation produced coatings whose corrosion resistance was increased by more than a factor of three.

Lithium Carbonate and Oxalate Salts as Corrosion Inhibitors for Magnesium Alloy AZ31 B in NaCl Solution

Corrosion Inhibition of AZ31-xLi (x = 4, 8, 12) Magnesium Alloys in Sodium Chloride Solutions by Aqueous Molybdate

Inhibiting Effect of Sodium Lignosulphonate on the Corrosion of AZ31 Magnesium Alloy in NaCl Solution

Lithium nitrate salt-assisted CO2 absorption for the formation of corrosion barrier layer on AZ91D magnesium alloy

Corrosion Inhibition of Magnesium Alloy in NaCl Solution by Ionic Liquid: Synthesis, Electrochemical and Theoretical Studies

Experimental and Theoretical Studies on Corrosion Inhibition Behavior of Three Imidazolium-Based Ionic Liquids for Magnesium Alloys in Sodium Chloride Solution

Inhibitive effect of sodium carbonate on corrosion of AZ31 magnesium alloy in NaCl solution

Corrosion Behaviour of Az31b Magnesium Alloy in Nacl Solutions Saturated with Co2

Effect of the Sodium Silicate Inhibitor on the Corrosion Protection of AZ31 Magnesium Alloy

A Combined Inhibiting Effect of Sodium Alginate and Sodium Phosphate on the Corrosion of Magnesium Alloy Az31 in Nacl Solution

Influence of chloride, sulfate and bicarbonate anions on the corrosion behavior of AZ31 magnesium alloy

The Effect of Vanadate, Phosphate, Fluoride Compounds on the Aqueous Corrosion of Magnesium Alloy AZ31 in Dilute Chloride Solutions

Corrosion Protection Behavior of Aluminate Ion-Loaded Layered Double Hydroxide Coating on AZ31 Magnesium Alloy

Corrosion Inhibition of AZ31 Magnesium Alloy in 3.5% NaCl by Green Corrosion Inhibitor: Maleic Hydrazide Derivative

Investigation of the inhibition effect of the environmentally friendly inhibitor sodium alginate on magnesium alloy in sodium chloride solution

Insight into Inhibition Behavior of Novel Ionic Liquids for Magnesium Alloy in NaCl Solution: Experimental and Theoretical Investigation

Corrosion Inhibition of Pure Mg Containing a High Level of Iron Impurity in Ph Neutral NaCl Solution

Corrosion Inhibition of Sodium Tannate for AZ61 Magnesium Alloy in Sodium Chloride Solution

Corrosion Inhibition of AZ31 Magnesium Alloy by Sodium Benzoate

Study of corrosion inhibitors on AZ91D magnesium alloy

Improving Environmental Adaptability and Long-Term Corrosion Resistance of Mg Alloys by Pyrazole Ionic Liquids: Experimental and Theoretical Studies