Influence of ammonium sulfate on the corrosion behavior of AZ31 magnesium alloy in chloride environment

Feng Ge,Zhongyu Cui,Yue Liu,Li Lei,Xin Wang,Hongzhi Cui

DOI: https://doi.org/10.1016/j.jma.2022.07.014

IF: 11.813

2022-09-23

Journal of Magnesium and Alloys

Abstract:Highlights • NH 4 + accelerates corrosion of AZ31 alloy in the Cl − -SO 4 2− system. • Buffering ability of NH 4 + is the dominant factor in NH 4 + -induced acceleration of AZ31 alloy. • High coverage of h ads generates an inductive loop within the low frequency range. • NH 4 + causes thinning and perforation of inner MgO layer and poriness of outer Mg(OH) 2 . • SO 4 2− helps to generate cracked but partially protective products and Cl − broadens the active corrosion area. Electrochemical corrosion of AZ31 magnesium alloy in the NH 4 + -SO 4 2− -Cl − environment is studied. Effect of NH 4 + overshadows that of Cl − as the (NH 4 ) 2 SO 4 concentration is 0.005 M or higher, yielding an evolution from localized corrosion to uniform corrosion. Acceleration effect of NH 4 + can be attributed to that (i) NH 4 + dissolves the inner MgO and hinders the precipitation of Mg(OH) 2 and (ii) the buffering ability of NH 4 + provides H + , enhances the hydrogen evolution, and expedites the corrosion process. The latter is demonstrated as the dominant factor with the results in unbuffered and buffered environments. The severe corrosion and hydrogen process in NH 4 + -containing solution results in a high H ads coverage and yields an inductive loop within the low frequency. Meanwhile, SO 4 2− is helpful in generating cracked but partially protective corrosion products, while Cl − could broaden the corrosion area beneath the corrosion product.

metallurgy & metallurgical engineering