Effect of NH4+ on the pitting corrosion behavior of 316 stainless steel in the chloride environment

Huiyun Tian,Lin Fan,Yizhou Li,Kun Pang,Fuzhen Chu,Xin Wang,Zhongyu Cui

DOI: https://doi.org/10.1016/j.jelechem.2021.115368

IF: 4.598

2021-08-01

Journal of Electroanalytical Chemistry

Abstract:Statistics analysis method is used to study the corrosion process of 316 stainless steel (316 SS) in NH4 +-containing environments. The pitting corrosion develops through three stages: nucleation, metastable pitting propagation and stable pitting propagation. The research results show that NH4 + does not significantly promote the nucleation process and the number of nucleation sites. However, the hydrolysis of NH4 + makes the solution weakly acidic and further slightly increases the degree of acidification of the solution, NH4 + can significantly promote the growth process of metastable pitting corrosion that has been formed. Positive shift potential can stimulate more active points on the surface of 316 SS, promote pitting initiation, and increase the nucleation number of metastable pitting. In the growth and propagation process of metastable pitting, the high applied potential can promote the rupture of the residual passive film above pits. In the process of stable pitting growth and propagation, the pit growth is controlled by diffusion and has nothing to do with applied potential and solution ions, and the pit growth is mainly along the depth direction.

chemistry, analytical,electrochemistry

What problem does this paper attempt to address?

The paper primarily explores the effect of ammonium ions (NH₄⁺) on the pitting behavior of 316 stainless steel in a chloride ion-containing environment. Specifically, the study focuses on the following aspects:

1. **Research Background**: 316 stainless steel has good corrosion resistance due to the protective passive film formed on its surface. However, this passive film is not completely uniform and dense, and relatively weak areas are prone to erosion, leading to pitting damage. Chloride ions (Cl⁻) are among the most aggressive ions in the service environment of stainless steel, capable of inducing pitting.

2. **Research Objective**: To study the effect of NH₄⁺ on the pitting behavior of 316 stainless steel in chloride ion-containing solutions using statistical analysis methods, particularly focusing on the three stages of pitting development: nucleation, metastable pitting propagation, and stable pitting propagation.

3. **Experimental Design and Methods**: Techniques such as electrochemical testing, confocal laser scanning microscopy (CLSM), and scanning electron microscopy (SEM) were used to study the effect of NH₄⁺ on the pitting behavior of 316 stainless steel at different potentials. The experiments used sodium chloride solutions containing NH₄⁺ as the test medium, and cyclic voltammetry was employed to determine the pitting potential (Epit) and protection potential (Eprot).

4. **Main Findings**:
- NH₄⁺ has no significant effect on the pitting nucleation process but can promote the growth of already formed metastable pits. The hydrolysis of NH₄⁺ makes the solution weakly acidic, further increasing the acidity of the solution, which favors the growth of metastable pits.
- High applied potentials can stimulate more active sites on the surface of 316 stainless steel, promoting pitting and increasing the number of metastable pitting nucleation sites.
- During the growth and propagation of metastable pits, high applied potentials can promote the rupture of the residual passive film on the pits.
- During the growth and propagation of stable pits, the growth of pits is diffusion-controlled, independent of the applied potential and solution ions, and the pits mainly grow in the depth direction.

In summary, this study aims to explore the specific mechanisms of NH₄⁺'s effect on the pitting behavior of 316 stainless steel through experimental and statistical analysis methods, providing a theoretical basis for understanding and predicting the corrosion behavior of such materials in specific environments.