Passivation behavior and surface chemistry of 316 SS in the environment containing Cl− and NH4+

Huiyun Tian,Feilong Sun,Fuzhen Chu,Liwei Wang,Xin Wang,Zhongyu Cui

DOI: https://doi.org/10.1016/j.jelechem.2021.115138

IF: 4.598

2021-04-01

Journal of Electroanalytical Chemistry

Abstract:The passivation behavior and surface chemistry of 316 stainless steel (316 SS) in the environment containing NH4 + and Cl− are studied systematically in this paper. The influence of NH4 + on the passive film formed on 316 SS in the presence of Cl− was studied by electrochemical testing, point defect model (PDM), and X-ray photoelectron spectroscopy (XPS). The results show that NH4 + is favorable for the passive film formed on 316 SS. According to the PDM, it is concluded that the film performance is affected by the defect density and the defect diffusion coefficient, while the addition of low concentration NH4 + has little influence on the defect density but reduces the defect diffusion coefficient to delay the dissolution of the passive film, increasing the corrosion resistance of the passive film. In addition, the XPS results show that the addition of NH4 + does not have much influence on the double-layer structure, but increases the contents of Fe(III) and Cr(OH)3 in the surface layer of the passive film, making the surface layer of the passive film denser and resistant to erosive ions.

chemistry, analytical,electrochemistry

What problem does this paper attempt to address?

The paper primarily explores the passivation behavior and surface chemical properties of 316 stainless steel (316 SS) in environments containing chloride ions (Cl⁻) and ammonium ions (NH₄⁺).

The core research questions of the paper are as follows:

1. **Factors Affecting the Performance of the Passivation Film**: Investigate the impact of NH₄⁺ on the performance of the passivation film formed on the surface of 316 SS, especially in the presence of Cl⁻.

2. **Analysis of the Structure and Composition of the Passivation Film**: Study the influence of NH₄⁺ on the formation process of the passivation film through electrochemical tests, point defect model (PDM), and X-ray photoelectron spectroscopy (XPS).

3. **Exploration of Corrosion Mechanisms**: Analyze how NH₄⁺ affects the stability of the passivation film and the corrosion behavior of stainless steel.

Specifically, the paper focuses on the following aspects:

- **Formation of the Passivation Film**: Investigate the conditions for the formation of the passivation film through potential polarization tests and analyze the performance of the passivation film, including its composition, structure, thickness, and semiconductor properties.

- **Mechanism of NH₄⁺ Action**: Study how NH₄⁺ affects the density and diffusion coefficient of defects in the passivation film, thereby influencing the dissolution rate of the passivation film and enhancing its corrosion resistance.

- **Surface Chemical Changes of the Passivation Film**: Use XPS technology to study the impact of NH₄⁺ on the composition of the surface layer of the passivation film (such as the content of Fe(III) and Cr(OH)₃) and how these changes make the surface of the passivation film denser and more resistant to aggressive ions.

In summary, this paper aims to comprehensively understand the behavior and characteristics of the passivation film on the surface of 316 SS under the combined action of NH₄⁺ and Cl⁻, thereby providing a theoretical basis for understanding the corrosion mechanisms of stainless steel in complex marine environments.